Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Production of beryllium copper pipe

A manufacturing method and copper tube technology, applied in the direction of manufacturing tools, other manufacturing equipment/tools, etc., can solve the problems of time-consuming, labor-intensive, low efficiency, etc., and achieve the effect of reducing costs

Inactive Publication Date: 2006-05-31
上海威嘉金属材料有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] If the manufacturer needs it, one is to rely on imports; another alternative is to use beryllium copper rods to cut into short pieces, and then use machine tools to drill and cut; such utilization is inefficient, time-consuming and labor-intensive; if required If the pipe is long or thin, there is nothing you can do

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The weight ratio is beryllium 2.0, phosphorus 0.1, copper balance, and impurities are less than or equal to 0.15. The beryllium copper ingot with the specification of Φ80mm×0.45mm×250mm is extruded on an 800-ton extrusion machine, and the heating temperature is 760-780° to form beryllium. Copper blank tube; annealed under the protection of H2 gas, the annealing temperature is 540-560 °, and then rapidly and strongly cooled to 15-35 °; after the tube is cooled and softened, it is rolled again, rolling speed and feeding amount: the speed is 95 times / min, the feeding rate is 2.5mm / min; after 4 stretches, the processing coefficient is controlled at 1.6;

Embodiment 2

[0014] Extrude beryllium-copper ingots with a diameter of 50mm, an inner hole of 30mm, a length of 210mm, a weight ratio of beryllium 0.2, phosphorus 0.2, copper balance, and impurities less than or equal to 0.15 through a 600-ton extrusion machine, and the heating temperature is 750-770 °, into beryllium copper blank tube; annealed under the protection of H2 gas, the annealing temperature is 500-520 °, and then rapidly and strongly cooled to 0-20 °; after the tube is cooled and softened, it is rolled again, rolling speed and feeding amount: The speed is 90 times / minute, and the feeding amount is 2mm / minute; after 3 stretches, the processing coefficient is controlled at 1.2;

Embodiment 3

[0016] Extrude beryllium-copper ingots with a diameter of 90mm, an inner hole of 50mm, a length of 300mm, a weight ratio of beryllium 2.5, phosphorus O, copper balance, and impurities less than or equal to 0.15 through an 800-ton extrusion machine, and the heating temperature is 780-800 °, into a beryllium copper rough tube; annealed under the protection of H2 gas, the annealing temperature is 580-600 °, and then rapidly and strongly cooled to 30-50 °; after the tube is cooled and softened, it is rolled again, the rolling speed and the feeding amount: The speed is 100 times / minute, and the feeding amount is 3mm / minute; after 10 stretches, the processing coefficient is controlled at 1.8.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A technology for manufacturing the beryllium-copper pipe includes such steps as providing a beryllium-copper alloy ingot prepared from Be, P and Cu and with 50-90 mm for diameter, 30-50 mm for internal hole diameter and 210-300 mm for length, extruding at 750-800 deg.C by (600-800)-ton press, annealing in H2 at 500-600 deg.C, forced cooling to 0-50 deg.C, and rolling.

Description

technical field [0001] The invention relates to a method for manufacturing a copper tube, in particular to a method for manufacturing a beryllium copper tube. Background technique [0002] Beryllium is a heavy metal element with strong and light properties. [0003] Beryllium copper tube is a high-performance tube material for oil exploration, high-end communication equipment, and high-demand pressure instrument production. It is characterized by strong corrosion resistance, wear resistance, high strength and high elasticity. [0004] At present, there are beryllium copper strips, rods, and wires among the similar beryllium copper tube products in China, but there are no beryllium copper tubes. [0005] If the manufacturer needs it, one is to rely on imports; another alternative is to use beryllium copper rods to cut into short pieces, and then use machine tools to drill and cut; such utilization is inefficient, time-consuming and labor-intensive; if required If the pipe i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P23/04C22C9/00
Inventor 方云冯蔚
Owner 上海威嘉金属材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com