Organic polysiloxane composition solidifying at room temperature
A polysiloxane, room temperature curing technology, used in other chemical processes, chemical instruments and methods, adhesives, etc., can solve the problem of inability to obtain mechanical properties, and achieve the effect of long operation time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0073] 100 parts by mass of dimethyl polysiloxane with a viscosity of 700 mPa·s blocked with hydroxyl groups at both ends, and a dimethyl polysiloxane with a viscosity of 700 mPa·s blocked with a trimethoxysilyl group connected by a silethylene group Composition 1 was prepared by adding 0.2 part by mass of tin dioctoate to 25 parts by mass of dimethylpolysiloxane and mixing uniformly.
Embodiment 2
[0075] Except that in Example 1, the addition amount of dimethylpolysiloxane with a viscosity of 700 mPa·s blocked with a trimethoxysilyl group through the connection of silethylene groups was 50 parts by mass. , Composition 2 was prepared in the same manner as in Example 1.
Embodiment 3
[0081] 35 parts by mass of dimethyl polysiloxane with a viscosity of 50,000 mPa·s blocked with hydroxyl groups at both ends, 40 parts by mass of colloidal calcium carbonate, and a compound with a viscosity of 100 mPa·s blocked with trimethylsiloxy groups at both ends Add 25 parts by mass of dimethylpolysiloxane and 20 parts by mass of dimethylpolysiloxane with a viscosity of 30,000 mPa·s blocked by trimethoxysilyl groups connected by silethylene groups at both ends Composition 4 was prepared by mixing 0.2 parts by mass of tin dioctoate evenly.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap