Non-metal inorganic powdery composite flame-proof material and its production method, and sheet and its production method

An inorganic powder and non-metal technology, which is applied in the field of composite non-combustible materials and its manufacturing, can solve the problems of environmental and personnel hazards, environmental protection, and inability to recycle, and achieves the effects of increasing bonding strength, low cost, and high mechanical properties.

Inactive Publication Date: 2006-12-27
袁新周
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] The first purpose of the present invention is to provide an environmentally friendly, safe, energy-saving and recyclable non-metal Inorganic powder composite non-combustible material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Weigh the following raw materials:

[0054] 100 mesh quartz sand powder (non-metallic inorganic powder) 55kg,

[0055] Modulus 3.1 neutral solid water glass (adhesive) 30kg,

[0056] 80 mesh mica slag (reinforcing material) 10kg,

[0057] 200 mesh sodium fluorosilicate (curing agent) 3.5kg,

[0058] Ethylene-acrylic acid copolymer (EAA phase solvent) 0.5kg,

[0059] Calcium stearate (lubricant) 1kg,

[0060] Then put the non-metallic inorganic powder into the high-speed mixer, stir and heat it to 110-120 ℃, make the non-metallic inorganic powder dehumidify and dry to a water content of less than 2%, add additives, modifiers, and reinforcing materials, stir and mix evenly to 120 ℃ unload the material into a high-speed cold mixer, add the binder when the temperature of the mixture reaches normal temperature, and stir at a high speed for 5 minutes to discharge the material to obtain a non-metallic inorganic powder composite non-combustible material.

[0061] The above...

Embodiment 2

[0063] Weigh the following raw materials:

[0064] 200 mesh vermiculite powder (non-metallic inorganic powder) 70kg,

[0065] Neutral solid water glass (adhesive) with modulus 3.1 10kg,

[0066] Ceramic fiber (reinforcing material) 8kg,

[0067] Polyethylene PE (reinforcing material) 5kg,

[0068] 100 mesh quartz powder (hardener) 3kg,

[0069] Polyacrylic acid (PAA phase solvent) 1kg,

[0070] Acrylate copolymer carboxylate (dispersant) 3kg,

[0071] Then put the non-metallic inorganic powder into a high-speed mixer, stir and heat it to 110-120 ° C, so that the non-metallic inorganic powder is dehumidified and dried to a water content of less than 2%, add additives, modifiers, and reinforcing materials. 120 ℃ unload to the high-speed cold mixer, add the binder when the temperature of the mixture reaches normal temperature, and stir at a high speed for 5 minutes to discharge the material, that is, the non-metallic inorganic powder composite non-combustible material.

[0...

Embodiment 3

[0074] Weigh the following raw materials:

[0075] The mixture of 200-mesh ceramic powder and 200-mesh perlite powder (non-metallic inorganic powder) 64kg, of which 200-mesh ceramic powder 32kg, 200-mesh perlite powder 32kg,

[0076] 20kg of neutral solid water glass (adhesive) with modulus 3.1,

[0077] 60 mesh mica slag (reinforcing material) 11kg,

[0078] 200 mesh sodium fluorosilicate (curing agent) 2.8kg,

[0079] Ethylene-acrylic acid copolymer (EAA phase solvent) 0.2kg,

[0080] Polytetrafluoroethylene micropowder (surfactant) 2kg,

[0081] Then put the non-metallic inorganic powder into the high-speed mixer, stir and heat it to 110-120 ℃, make the non-metallic inorganic powder dehumidify and dry to a water content of less than 2%, add additives, modifiers, and reinforcing materials, stir and mix evenly to 120 ℃ unload the material into a high-speed cold mixer, add the binder when the temperature of the mixture reaches normal temperature, and stir at a high speed f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
modulusaaaaaaaaaa
Login to view more

Abstract

The invention relates the non-metal inorganic powder composite non-inflammable material and preparing method, sheet material and preparing method. The material comprises 55-70% non-metal inorganic powder, 10-30% binder, 10-15% reinforced materials, 2-4% auxiliary agent and 1-3% modifier. The method comprises the following steps: putting the non-metal inorganic powder into mixing machine, stirring, adding reinforced materials, auxiliary agent and modifier, stirring to 120Deg.C, putting them into cooling mixing machine, stirring to normal temperature, adding binder, and getting the product. The preparing method of sheet material comprises the following steps: heating the non-metal inorganic powder composite non-inflammable material by extrusion machine, squeezing with forming die, rolling, and getting the product. The invention has the advantages of low cost, environment protection, safety, and high mechanical energy. The product can be used in ship, marine drilling platform, battleship, furniture, nonbearing wall and baffle wall.

Description

technical field [0001] The present invention relates to a composite non-combustible material and a manufacturing method thereof, a composite non-combustible plate and sheet produced from the composite non-combustible material and a manufacturing method thereof. Background technique [0002] Non-combustible materials and their composite non-combustible plates and sheets are mainly used in the decoration of living, working, resting and entertainment cabins on ships, offshore platforms, and warships; clean room decoration, furniture, and non-load-bearing walls and partition walls in buildings. The current status of the above fields is briefly introduced as follows: [0003] 1. At present, the thermal insulation and fireproof materials and decorative materials (siding, ceiling, fire doors, sanitary units, etc.) used in the living, working, resting, entertainment, storage and other cabins of ships, offshore platforms, warships, etc. There are different effects, and the analysis ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K21/14C09K21/02
Inventor 袁新周
Owner 袁新周
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap