Testing apparatus and method of deriving young's modulus from tensile stress/strain relationships

Abstract

A method of testing and a tester apparatus to determine the axial stress and strain of cements under the temperature and pressures encountered by cement during use in wellbore environments. Using these stress and strain measurements, the Young's Modulus may be established for a material at the encountered temperature and pressure of the wellbore. By combining static tensile strength testing and elasticity measurements of cements, Young's Modulus values for different cement compositions under stresses that are similar to the conditions occurring in an actual wellbore are possible.

Description

FIELD OF THE INVENTION [0001] The invention relates to testing methods and devices used for testing of the mechanical properties of cement including cement formed in wellbore environments. BACKGROUND OF THE INVENTION [0002] Cement is used in the casing and liners of a wellbore. The annular space between the casing / lining and the wellbore is filled with a predetermined quantity of a cement mixture, which after hardening retains the casing / liner in place in the wellbore. The cement mixture is pumped in at the top end of the casing or liner, down to the lower end thereof and out into and up the annular space on the outside of the casing / liner. [0003] Cementing is employed during many phases of wellbore operations. For example, cement may be employed to cement or secure various casing strings and / or liners in a well. Cementing may also be used to repair casing and / or to achieve formation isolation. Additionally, cementing may be employed during well abandonment. Cement operations perfor...

AI Technical Summary

Benefits of technology

"The present invention offers a method and apparatus for testing the stress and strain of cements used in wellbore environments. This allows for the quantification of the mechanical properties of cements under the encountered temperature and pressure of the wellbore. The invention overcomes the problem of conventional static testing methods that are time-consuming and only test in compression. The testing apparatus allows for a more accurate testing of mechanical properties of cements to ensure the long-term integrity of the cement sheath in a well bore for the entire operation life of a given well. The invention also provides for real-time stress versus strain plots, data consistency and reliability, and multi-functionality for measuring cement shear bond strength while maintaining confining pressure and temperature."

Problems solved by technology

Cement operations performed in wellbores under these high stress conditions present problems including difficulty in obtaining wellbore isolation and maintaining the mechanical integrity of the wellbore.

Once established, this isolation may be impacted by the particular stresses associated with the environment found in the wellbore during operations.

Furthermore, well cement compositions may be brittle when cured.

These cement compositions may fail due to tensional and compressional stresses that are exerted on the set cement.

Relatively high temperatures may induce stress conditions and / or relatively high fluid pressures encountered inside cemented wellbore pipe strings during operations such as perforating, stimulation, injection, testing, or production.

In addition, variations in temperature and internal pressure of the wellbore pipe string may result in radial and longitudinal pipe expansion and / or contraction which tends to place stress on the annular cement sheath existing between the outside surface of a pipe string and the inside formation surface or wall of a wellbore.

In other cases, cements placed in wellbores are subjected to mechanical stress induced by vibrations and impacts resulting from operations.

The following testing method fail to provide a method of testing under these conditions.

This testing method therefore fails to simulate the stresses encountered in the higher temperature and pressure conditions of the wellbore environment.

This testing method therefore also fails to simulate the stresses encountered in the higher temperature and pressure conditions of the wellbore environment.

Tensile failure occurs rather than compressive failure because the areas of load application are in a state of triaxial compression.

This testing method therefore fails to simulate the stresses encountered in the higher temperature and pressure conditions of the wellbore environment.

None of these testing methods provides for the creation of samples under the temperature and pressure conditions found in a wellbore environment.