Water soluble two-component inorganic zinc paint and its making process

A two-component, inorganic zinc technology is used in the anti-corrosion of steel structures, water-based two-component inorganic zinc coatings and their manufacture, and the protection of high-strength bolted surfaces. Rough surface, less heat consumption and strong adhesion

Inactive Publication Date: 2008-01-30
上海暄能工程材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above-mentioned anti-slip coatings all solve the problem of the bolted joint surface through organic coatings, which have volatilization of organic solvents during production and use, causing harm to the environment, production and construction personnel, while water-based inorganic Zinc coatings could revolutionize this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A component:

[0014] 10 grams of polyethylene glycol, 49.5 grams of sodium silicate solution, 20 grams of nano-silica colloidal solution, and 2 grams of ethyltrimethoxysilane are dropped into a four-necked flask equipped with a stirrer and a condenser tube, and the temperature is raised with high-speed stirring. React at 95 DEG C for 3.5 hours, after cooling to room temperature, to obtain a gel, add 3 grams of sodium hydroxide, 13 grams of pure water, 0.1 grams of water-based defoamer CF-16 (produced by Blackburn Chemicals Ltd.Co.) and 2.4 grams Silica, milled for 1 hour, the resulting mixture is the A component of the paint.

[0015] B component:

[0016] Put 10 grams of flaky zinc powder, 7 grams of titanium-iron powder, 1 gram of wetting and dispersing agent DAP-C (produced by Beijing Tsinghua Yongchang Chemical Co., Ltd.), and 82 grams of spherical zinc powder into the stirrer, stir for 1 hour, and mix evenly. The resulting mixture is the B component of the paint...

Embodiment 2

[0019] A component:

[0020] 25 grams of polyethylene glycol, 24.7 grams of potassium silicate solution, 20 grams of nano-alumina colloidal solution, and 10 grams of chlorotrimethylsilane are dropped into a four-necked flask equipped with a stirrer and a condenser, stirred at a high speed, and heated at room temperature Reaction 8 hours, aging obtains gel, adds 2 gram ammoniacal liquors, 15 gram pure waters, 0.3 gram water-based defoamer CF-246 (produced by Blackburn Chemicals Ltd.Co.), 3 gram barium sulfate grinds 1 hour, obtains The mixture is the A component of the paint.

[0021] B component:

[0022] 14 grams of flake zinc powder, 5 grams of phosphorus iron powder, 0.1 gram of wetting and dispersing agent DAP-C (produced by Beijing Tsinghua Yongchang Chemical Co., Ltd.), and 80.9 grams of spherical zinc powder are dropped into the stirrer, stirred for 1 hour, and mixed uniformly. The resulting mixture is the B-component of the paint.

[0023] When using, mix component ...

Embodiment 3

[0025] A component:

[0026] 5 gram polyethylene glycol, 38 gram potassium silicate solution and 31 gram nano-silica colloidal solution, 10 gram methyltrimethoxysilane are put into the four-necked flask that agitator and condensing pipe are equipped with, high-speed stirring heats up, in React at 95°C for 5 hours, after cooling to room temperature, a gel was obtained, add 5 grams of potassium hydroxide, 10.7 grams of pure water, 0.3 grams of water-based defoamer CF-246 (produced by Blackburn Chemicals Ltd.Co.), and grind for 1 hours, the resulting mixture is the A component of the paint.

[0027] B component:

[0028] 25 grams of flake zinc powder, 25 grams of mica powder, 0.5 gram of wetting and dispersing agent DAP-C (produced by Beijing Tsinghua Yongchang Chemical Co., Ltd.), and 49.5 grams of spherical zinc powder are dropped into the stirrer, stirred for 1 hour, and mixed uniformly to obtain The mixture is the B component of the paint.

[0029] When using, mix componen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The water soluble inorganic zinc paint consists of two components, component A and component B, in the weight ratio of 1 to 1.5-4. The component A is prepared through mixing alkali silicate, water soluble resin, nano colloid solution of inorganic oxide and silane as cross-liking agent under stirring for reaction to obtain sol; ageing the sol to obtain gel; adding pure water, inorganic pigment, alkali water solution and water soluble defoaming agent; and grinding. The component B is prepared with spherical zinc powder, chip metal powder, alkali-resisting inorganic pigment and stuffing, wetting carboxylate dispersant and through mixing. The paint has good early stage water resistance, high slipping resistance and high salt mist corrosion resistance, and the production process has no waste water, slag and waste gas produced and is environment friendly.

Description

technical field [0001] The invention relates to a water-based paint and a manufacturing method thereof, in particular to a water-based two-component inorganic zinc paint and a manufacturing method thereof. The paint is especially suitable for the protection of high-strength bolt connection surfaces, and can also be widely used in the anticorrosion of steel structures. Background technique [0002] Water-based inorganic zinc-rich coatings are one of the few excellent coatings that can protect steel structures and make their corrosion resistance life exceed 10 years. It achieves the purpose of anti-corrosion through electrochemical action, that is, anode action. Its coating film is very hard and wear-resistant, has excellent chemical corrosion resistance within a certain pH value range, and can withstand high temperatures up to 400 °C. It can be used either as a single long-lasting protective coat or as a primer for high-performance paint systems. Since the 1970s, it has been...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D171/08C09D5/00
Inventor 汪国庆汪庆锋胡晶
Owner 上海暄能工程材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com