Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Flax blended spinning preparation process

A production process and technology of blended yarn, which is applied in the direction of yarn, bleached products, textiles and papermaking, etc., can solve the problems of hard hand feeling, no smooth feeling, no luster, etc., and achieve simple production process, good appearance gloss and smooth hand feeling Effect

Active Publication Date: 2010-02-24
ZHEJIANG JINYUAN FLAX
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pure flax yarn has rough appearance, uneven evenness, poor spinnability, monotonous color, no luster, hard hand feeling and no smooth feeling.
At the same time, there are certain technical difficulties in spinning high-count yarns from pure flax

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flax blended spinning preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] see figure 1 , comb long flax fibers into slivers of about 18cm, and make the slivers go through multiple drawing processes: the first drawing, the second drawing, the third drawing, and the fourth drawing The flax fiber is continuously drafted and combined in the process, and bamboo fiber is mixed in the fifth drawing process. The bamboo fiber is uniform in length, accounting for 8% of the blended yarn mass percentage, and the bamboo fiber is drawn and combined with the hemp strip. Made into roving. The roving is scoured and bleached, and the scoured and bleached process includes two processes of sub-bleaching and oxygen bleaching, and the sodium chlorite NaCLO of 1.5g / L is added in water earlier. 2 , the pH value is 2.5, the initial temperature is 30°C, it takes 30 minutes to raise the temperature to 50°C, keep warm for 30 minutes, wash with water, then carry out oxygen bleaching, add 3.5g / L hydrogen peroxide H 2 o 2 , pH value 10, initial temperature: 50°C, take 3...

Embodiment 2

[0010] see figure 1 , comb long flax fibers into slivers of about 18cm, and make the slivers go through multiple drawing processes: the first drawing, the second drawing, the third drawing, and the fourth drawing The flax fiber is continuously drafted and combined in the process, and bamboo fiber is mixed in the fifth drawing process. The bamboo fiber is uniform in length, accounting for 40% of the blended yarn mass percentage, and the bamboo fiber is drawn and combined with the hemp sliver. Made into roving. The roving is scoured and bleached, and the scoured and bleached process includes two processes of sub-bleaching and oxygen bleaching, and the sodium chlorite NaCLO of 1.5g / L is added in water earlier. 2 , the pH value is 3, the initial temperature is 30°C, it takes 30 minutes to raise the temperature to 50°C, keep warm for 40 minutes, wash with water, then carry out oxygen bleaching, add 3.5g / L hydrogen peroxide H 2 o 2 , pH value 10, initial temperature: 50°C, take 3...

Embodiment 3

[0012] see figure 1 , comb long flax fibers into slivers of about 18cm, and make the slivers go through multiple drawing processes: the first drawing, the second drawing, the third drawing, and the fourth drawing The flax fiber is continuously drafted and combined in the process, and bamboo fiber is mixed in the fifth drawing process. The bamboo fiber is uniform in length, accounting for 75% of the blended yarn mass percentage, and the bamboo fiber is drawn and combined with the hemp strip. Made into roving. The roving is scoured and bleached, and the scoured and bleached process includes two processes of sub-bleaching and oxygen bleaching, and the sodium chlorite NaCLO of 1.5g / L is added in water earlier. 2 , the pH value is 3.5, the initial temperature is 30°C, it takes 30 minutes to raise the temperature to 50°C, keep warm for 25 minutes, wash with water, then carry out oxygen bleaching, add 3.5g / L hydrogen peroxide H 2 o 2 , pH value 10.5, initial temperature: 50°C, tak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing flax blended yarn used in clothes and face fabric, comprising that: preparing flax long fiber into flax bars; combing bars via at least five processes; adding bamboo fibers into combining process, while the bamboo fibers are 8-75mass% of total blended yarn mass; combing them and drawing to prepare rove; boiling and bleaching the rove; spinning into spun yarn; drying, coiling and shaping. The invention has simple process, while the product has uniform bars, beautiful appearance and smooth surface.

Description

technical field [0001] The invention relates to a weaving method, in particular to a production process of flax blended yarn used for clothing and home textile fabrics. Background technique [0002] Flax is a rare natural species. Natural flax fiber has strong hygroscopicity, good heat dissipation and air permeability, anti-mildew and moth resistance, no static electricity, no chemical components, and unique characteristics of inhibiting bacterial growth and effectively blocking ultraviolet penetration. The world is known as the "Fiber Queen". However, pure flax spun yarn has rough appearance, uneven evenness, poor spinnability, monotonous color, no luster, hard hand and no smooth feeling. At the same time, there are certain technical difficulties in spinning high-count yarns from pure flax. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art and provide a production process of fl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D06L3/14D06L3/08D06L3/02D06L4/13D06L4/24
Inventor 沈跃明
Owner ZHEJIANG JINYUAN FLAX
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com