Mine-well engineering material for pit-wood sleeper and preparing method therefor

A technology of engineering materials and sleepers, which is applied in the field of mine engineering materials for pit wood sleepers and its preparation, can solve the problems of low safety factor, difficult construction, easy corrosion, etc., and achieve the effects of reducing mine cost, low cost and prolonging service life

Inactive Publication Date: 2007-11-14
王章安
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Human beings need energy to dig underground mineral deposits. For a long time, most of the materials used in the mining process are wood and Portland cement materials. The basic national policy of deforestation is repeatedly ordered; on the other hand, ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The invention includes a bamboo tendon skeleton, which mainly contains the following components: by weight, 10 parts of magnesium oxide, 5 parts of magnesium chloride, 10 parts of sawdust, 5 parts of hemihydrate gypsum, 1 part of plastic fiber, ferrous sulfate 1 part, 1 part oxalic acid, 30 parts water.

[0017] Preparation method of mine engineering material for pit wood sleepers:

[0018] A. According to the ratio of the above ingredients, first dissolve the magnesium chloride, gypsum hemihydrate, ferrous sulfate and oxalic acid in the formula into water, and then add this solution to the mixer;

[0019] B. Add magnesia, sawdust, and plastic fibers into the above-mentioned mixer according to the above-mentioned raw material formula, and form a slurry after stirring;

[0020] C, put the bundled bamboo tendon skeleton into the mould;

[0021] D, the above-mentioned stirred slurry is added to the mold of the bamboo rib skeleton, and the slurry is filled with the mold a...

Embodiment 2

[0023] The invention includes a bamboo tendon skeleton, which mainly contains the following components: by weight, 20 parts of magnesium oxide, 10 parts of magnesium chloride, 20 parts of sawdust, 10 parts of hemihydrate gypsum, 2 parts of plastic fiber, ferrous sulfate 3 parts, 1.5 parts of oxalic acid, 40 parts of water.

[0024] Also include 5 parts of rice husk grains, 5 parts of alarite and 1 part of hair section in the component of the present invention.

[0025] The preparation method of the mine engineering material for pit wood sleepers is the same as above.

Embodiment 3

[0027] The invention includes a bamboo tendon skeleton, which mainly contains the following components: by weight, 50 parts of magnesium oxide, 15 parts of magnesium chloride, 25 parts of sawdust, 15 parts of hemihydrate gypsum, 3 parts of plastic fiber, ferrous sulfate 5 parts, 2 parts oxalic acid, 40 parts water.

[0028] Also include 12 parts of rice husk grains, 8 parts of alarite, and 2 parts of hair section in the component of the present invention.

[0029] The preparation method of the mine engineering material for pit wood sleepers is the same as above.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention relates to a shaft engineering material used for pitprop and crosstie, mostly includes bamboo reinforcement skeleton. According to weight the bamboo reinforcement skeleton includes follow components: magnesia 10 to 80 shares, magnesium chloride 5 to 30, wood flour 10 to 50, semi-hydrated gypsum 5 to 20, plastic fibre 1 to 5, ferrous sulfate 1 to 10, oxalic acid 1 to 3, water 30 to 60 shares. This invention also relates to the preparation method. This invention can effectively avoide insufficiency of traditional stuff such as perishable, flammability and easy exploding, also possess unique merits such as ageing resistance corrosion prevention, fireproofing, waterproof and be able to saw and cut and so on in the moist roadway environment.

Description

technical field [0001] The invention relates to an inorganic mine support material, in particular to a mine engineering material for pit wood sleepers and a preparation method thereof. Background technique [0002] China is a large natural country rich in underground mineral deposits. Since the mining of underground mineral deposits, wood and cement products have been used as underground roadway support and track bedding. In recent years, metal products have also been used as supports, while wood is perishable, flammable, explosive, and has a short pressure-bearing time; cement products have a large proportion, are difficult to construct, and are brittle and easy to crack, making them difficult to replace. The cost of metalwork is high and it is inconvenient to hang cables. [0003] Throughout the history of the world, energy has been a long-term need of mankind. Human beings need energy to dig underground mineral deposits. For a long time, most of the materials used in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/32C04B18/26C04B16/06C04B30/02C04B22/14C04B24/04
CPCC04B28/32C04B2111/00724Y02W30/91C04B14/202C04B16/06C04B18/248C04B18/26C04B18/265C04B22/143C04B22/149C04B24/04C04B40/0028C04B40/0067C04B40/02C04B22/142C04B32/02
Inventor 王章安王红亮李三重
Owner 王章安
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap