Burrow stone imitation ceramic tile and preparation method thereof

A technology of imitating travertine and ceramic tiles, applied in the field of ceramic tiles, can solve the problems of inability to be used as decorative materials, difficult to control production, and small holes.

Active Publication Date: 2008-02-13
DONGGUAN CITY WONDERFUL CERAMICS IND PARK
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantages are: the holes are small and cannot be used as decorative materials
Its shortcoming is: this method production is difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The formula (percentage by weight) of the low-temperature material is as follows: clay: 5%-25%, porcelain sand: 0.1%-40%, talc: 0.1%-20%, fluorite: 20%-90%. The low-temperature material is spray-dried into powder by ball milling. As a molding material, it is molded together with other ceramic powders, then dried, fired, and polished; after polishing, these holes are used as decorative effects.

Embodiment 2

[0035] The formula (percentage by weight) of the low-temperature material is: clay: 5% to 25%, porcelain sand: 0.1% to 20%, and frit 50% to 90%. The low-temperature material is powdered by ball milling and used as a molding material, Other ceramic powders are formed together, then dried, soaked, fired, scraped (ground), the surface layer is removed to fill the holes with resin materials, and then polished to achieve the decorative effect of imitating travertine and then polishing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to View More

Abstract

The present invention discloses an imitated hole stone ceramic tile and the corresponding preparation method, which can produce the hole decoration effect with random change, different and various shape and depth. The molding material in the imitated hole stone ceramic tile includes a low-temperature material at least; the molar percent of the material component is as follow: 5-25 percent of mud; 0.1-40 percent of ceramic sand; 0.1-20 percent of steatite; 20-90 percent of fluorite. The low temperature material is mixed with a ceramic powder for molding through a ball-grilling and spraying drying powder material, and then to be dried, baked and polished; after being polished, the hole can be used as the decorating material. Or, the molding material in the imitated hole stone ceramic tile includes a low-temperature material at least; the molar percent of the material component is as follow: 5-25 percent of mud; 0.1-20 percent of ceramic sand; 50-90 percent of melting block. The low temperature material is mixed with a ceramic powder for molding through a ball-grilling and spraying drying powder material, and then to be dried, flower-designed, baked and smoothed as well as to wide off the surface for being filled with the hole so as to realize the effect of imitating and repairing the hole first and polishing latter.

Description

technical field [0001] The invention relates to a ceramic tile, in particular to a travertine-imitation ceramic tile capable of generating randomly variable, different-shaped, and different-depth hole decoration effects and a preparation method thereof. Background technique [0002] Chinese patent CN01814404.7 announced "honeycomb ceramic structure and its manufacturing method". Its purpose is to achieve low pressure loss and high collection efficiency. Its chemical composition is composed of SiO2 42-56 wt%, Al2O3 30-45 wt%, MgO 12-16 wt%, and the crystal phase is mainly composed of cordierite The ceramic honeycomb structure has a porosity of 55-65%, an average pore diameter of 15-30 μm, and the total area of ​​the pores exposed on the surface of the partition wall constituting the honeycomb ceramic structure is 35% of the total area of ​​the surface of the partition wall above. Its disadvantage is that the holes are small and cannot be used as decorative materials. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13
Inventor 黄建平范建辉文武洪庆复
Owner DONGGUAN CITY WONDERFUL CERAMICS IND PARK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com