Method for preparing high concentration water-coal-slurry by low-rank coal

A high-concentration water, low-rank coal technology, applied in combustion methods, block/powder fuel preparation, combustion equipment, etc., can solve problems such as long processing time and high processing temperature, improve particle size distribution and reduce preparation energy. consumption effect

Active Publication Date: 2010-07-14
CHINA COAL RES INST CCRI ENERGY SAVING TECH CO LTD
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can effectively improve and subsequently reduce the water content of low-rank coal, but this method adopts higher treatment temperature and longer treatment time, which is contrary to the lower temperature and shorter time required by industrialization , thus limiting the wide use of low-rank coal in the preparation of high-concentration coal-water slurry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high concentration water-coal-slurry by low-rank coal
  • Method for preparing high concentration water-coal-slurry by low-rank coal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The low-rank raw coal used in this example is Shangwan coal with a water content of 7.5%. The process of utilizing this coal to prepare high-concentration coal-water slurry is as follows:

[0030] (1) Ultra-fine crushing of Shangwan coal until the coal particle size reaches 1mm;

[0031] (2) Mix the crushed Shangwan coal particles with water in a mass ratio of 7:3, and then send the mixture into a coarse grinder for wet coarse grinding, so that the particle size of the coal particles in the coal slurry formed at the outlet of the coarse grinder ≤800μm, coal particle size less than 75μm in the coal slurry accounts for more than 60% of the total mass of dry coal;

[0032] (3) Mix 20% of the coal slurry flow at the outlet of the coarse mill with water in a mass ratio of 10:3, and then send the mixture into the fine mill for wet fine grinding, so that the coal in the coal slurry at the outlet of the fine mill Particle size≤20μm;

[0033] (4) 50% of the coal slurry amount...

Embodiment 2

[0039] The low-rank raw coal used in this example is Chifeng coal with a water content of 14%. The process of utilizing this coal to prepare high-concentration coal-water slurry is as follows:

[0040] (1) Superfinely crush Chifeng coal until the coal particle size reaches 1mm;

[0041] (2) Mix the crushed Chifeng coal particles with water in a mass ratio of 6:4, and then send the mixture into a coarse grinder for wet coarse grinding, so that the particle size of the coal particles in the coal slurry formed at the outlet of the coarse grinder is ≤ 1000μm, coal particle size less than 75μm in the coal slurry accounts for more than 50% of the total mass of dry coal;

[0042] (3) Mix 10% of the coal slurry flow rate at the outlet of the coarse mill with water in a mass ratio of 5:1, and then send the mixture into the fine mill for wet fine grinding, so that the coal in the coal slurry at the outlet of the fine mill Particle size≤20μm;

[0043] (4) The coal slurry after the wet...

Embodiment 3

[0048]The low-rank raw coal used in this example is Halagou coal with a water content of 5%. The process of utilizing this coal to prepare high-concentration coal-water slurry is as follows:

[0049] (1) Carry out ultra-fine crushing of the Halagou coal until the coal particle size reaches 1mm;

[0050] (2) Mix the broken Halagou particles with water in a mass ratio of 8:2, and then send the mixture into a coarse grinder for wet coarse grinding, so that the particle size of the coal particles in the coal slurry formed at the outlet of the coarse grinder ≤800μm, coal particle size less than 75μm in the coal slurry accounts for more than 60% of the total mass of dry coal;

[0051] (3) Mix 30% of the coal slurry flow rate at the outlet of the coarse mill with water in a mass ratio of 5:2, and then send the mixture into the fine mill for wet fine grinding, so that the coal in the coal slurry at the outlet of the fine mill Particle size≤15μm;

[0052] (4) The coal slurry after t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method of utilizing low-rank coal to prepare high concentration coal water slurry, which comprises the following steps: step one, super-fine smashup is operated to the low-rank coal; step two, coal particles after being smashed up are mixed with water according to the mass proportion of 6 to 8: 4 to 2; step three, the wet rough grinding is operated to mixture; step fourth, (1), 10 to 30 percent of total weight of the coal water slurry after being roughly ground is mixed with the water according to the mass proportion of 5:1 to 2, and then the wet fine grinding is operated to the mixture; (2), except the coal water slurry after being finely ground in a wet type, the coal water slurry after being roughly ground in a wet type is delivered into a filtering device; step five, the coal water slurry after being finely ground in the step four (1) is treated according to the following way: (1), all coal water slurry is returned to step three to be circularly and roughly ground or (2) the partial coal water slurry is returned to step three to be circularly and roughly ground, and the other part coal water slurry after being finely ground is directly delivered intothe filtering device; or (3) all coal water slurry is directly delivered into the filtering device; six step, the coal water slurry delivered into the filtering device is filtered by a filtering net with 18 to 20 meshes, the coal water slurry is stirred in high gear and then stewed, or the coal water slurry is stirred in low speed to obtain the high concentration coal water slurry product.

Description

technical field [0001] The invention relates to a method for preparing coal-water slurry, in particular to a method for preparing high-concentration coal-water slurry by using low-rank coal. Background technique [0002] At present, international oil prices remain high, and fuel resources are increasingly in short supply, and coal-water slurry is an ideal substitute for fuel oil. The concentration and particle size of coal water slurry directly affect the effect of coal water slurry replacing fuel oil. In the preparation process of coal water slurry, the pulping process plays a very important role. The quality of the pulping process directly affects the final preparation concentration of coal water slurry and the energy consumption and cost of pulping. To prepare high-concentration coal-water slurry by conventional pulping process, it is often necessary to select coal types that are easy to slurry (low water content), and low-rank coal, which accounts for the largest propor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F23K1/02
Inventor 何国锋段清兵王国房贾传凯梁兴纪磊刘解王秀月
Owner CHINA COAL RES INST CCRI ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com