Preparation of nano silicon dioxide lubricating grease

A technology of nano-silica and lubricating grease, applied in lubricating compositions, petroleum industry, additives, etc., can solve the problems of large particle size and poor stability, and achieve small mass loss, excellent high-temperature performance, and good shear stability Effect

Inactive Publication Date: 2008-08-13
益田润石(北京)化工有限公司
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These early nano-silicas are all laboratory prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] Preparation of nano-silica grease of the present invention

[0030] A certain amount of silicone oil was weighed, heated to 150°C, and kept at a constant temperature for 5min. At this temperature, add the modifier, the content of which is 20% by mass of the silica, and stir until the modifier is uniformly dispersed in the base oil. Stirring was continued to raise the temperature to 157°C. Constant temperature for 5min. Stop heating, add nano-silica, and stir well. Grind twice with a three-roll mill to form grease.

Example Embodiment

[0031] Example 2

[0032] Preparation of nano-silica grease of the present invention

[0033] A certain amount of silicone oil was weighed, heated to 132°C, and kept at a constant temperature for 5min. At this temperature, add the modifier, the mass of which is 10% of the mass of silica, and stir until the modifier is uniformly dispersed in the base oil. Stirring was continued to raise the temperature to 140°C. Constant temperature for 5min. Stop heating, add nano-silica, and stir well. Grind twice with a three-roll mill to form grease.

Example Embodiment

[0034] Example 3

[0035] Preparation of nano-silica grease of the present invention

[0036] A certain amount of silicone oil was weighed, heated to 120°C, and kept at a constant temperature for 5min. At this temperature, add the modifier, the mass of which is 5% of the mass of silica, and stir until the modifier is uniformly dispersed in the base oil. Stirring was continued to raise the temperature to 130°C. Constant temperature for 5min. Stop heating, add nano-silica, and stir well. Grind twice with a three-roll mill to form grease.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of high-performance silicon dioxide grease, which comprises the following components, base oil of 70 to 90 weight percent, silica of 5 to 30 weight percent, modifying agent is in a dose of 5-30 weight percent of the silicon dioxide. The silicon dioxide grease of the invention has a very good storage stability and shear stability, good colloidal stability, water resistant properties of high temperature and low temperature performance. The silicon dioxide grease can be used for electrical insulation, damping system lubrication, vacuum sealed, instruments and cock sealing and lubricating, can also be used for resistant chemical media site lubricating and sealing, and so on. In addition, the silicon dioxide grease can also be used for preparing valves grease, methanol resistance grease, and is applicable in lubrication and interrupter of the metal contact of switch silvering, silver plating, and tinning and other.

Description

technical field [0001] The invention relates to an effective sealing grease, which is a nano-silica lubricating grease with excellent storage stability and shear stability, and a nano-silica lubricating grease with obvious progress in water resistance, high and low temperature, and colloidal stability. Silica lubricating greases, in particular to the preparation and determination of the properties of such greases. Background technique [0002] With the rapid development of modern industry, the industrial production department has put forward increasingly strict requirements on the performance of grease in many aspects such as high temperature resistance, extreme pressure and wear resistance, water resistance, protection, and bearing life. At present, the general trend of the development of lubricating grease is multi-efficiency and high dropping point, so as to meet the lubrication requirements of modern mechanical parts. The development of high dropping point lubricating g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M139/04C10M125/26C10N30/00C10N40/34
Inventor 王金波于海英杜守琴甄轶黄学东黄学智
Owner 益田润石(北京)化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap