A collagen cross-linking and cross-linking modification technology, applied in medical science, prostheses, etc., can solve the problems of cytotoxicity and difficult-to-control degradation, achieve easy cross-linking, improve mechanical properties, and control cross-linking Effect

Inactive Publication Date: 2011-04-20
SICHUAN UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Common chemical cross-linking methods are cytotoxic, and physical cross-linking methods are difficult to control its degradation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical grade reconstructed collagen cross-linking modified method
  • Medical grade reconstructed collagen cross-linking modified method
  • Medical grade reconstructed collagen cross-linking modified method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Add 1ml of potassium phosphate solution with a concentration of 0.1mol / L to 5ml of uniform collagen solution with a concentration of 5mg / ml at a temperature of 15°C and slowly stir, adjust the pH of the mixed solution to 7.0 with an acid or alkali solution, and mix The solution is kept at a temperature of 25°C and a humidity of 50%, and it is allowed to stand for 6 hours to make it into a uniform colloid. After the colloid is placed in an environment of -20°C and -60°C for 24 hours, it is dehydrated in a freeze dryer to obtain ions Crosslinked Modified Reconstituted Collagen.

Embodiment 2

[0034] Add 5ml of sodium phosphate solution with a concentration of 0.5mol / L to 25ml of a uniform normal collagen solution with a concentration of 10mg / ml at a temperature of 20°C and slowly stir, adjust the pH of the mixed solution to 8.5 with an acid or alkali solution, and mix The solution is kept at a temperature of 40°C and a humidity of 70%, and it is allowed to stand for 12 hours to make it into a uniform colloid. After the colloid is placed in an environment of -40°C and -80°C for 48 hours, it is dehydrated in a freeze dryer to obtain ions Crosslinked Modified Reconstituted Collagen.

Embodiment 3

[0036] Add 2ml of dipotassium hydrogen phosphate solution with a concentration of 0.2mol / L to 10ml of ordinary collagen solution with a uniform concentration of 6mg / ml at a temperature of 16°C and slowly stir, and adjust the pH value of the mixed solution to 7.2 with acid or alkali solution , the mixed solution is kept at a temperature of 28°C and a humidity of 55%, and it is left to stand for 8 hours to make it into a uniform colloid. Obtain ionically cross-linked modified collagen.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for cross-linking and modifying medical-grade reconstructed collagen, which is characterized in that 1 to 5 weight parts of phosphate solution with the concentration of 0.1 mol / L to 0.5mol / L is added into 5 to 25 weight parts of uniform regular collagen solution with the concentration of 5 mg / ml to 10mg / ml at the temperature of 15 DEG C to 20 DEG C while slowly stirring. Acid solution or aqueous alkali is used for adjusting the pH value of the mixed solution to 7.0 to 8.5. The mixed solution stands for 6 hours to 12 hours at the temperature of 25 DEG C to 40 DEG C and humidity of 50 percent to 70 percent so as to form uniform colloid. The colloid is sequentially arranged in the environment of minus 20 DEG C to minus 40 DEG C and minus 60 DEG C to minus 80 DEG C to be frozen for 24 hours to 48 hours, and then dehydrated in a lyophilizer to obtain the reconstructed collagen with cross-linked and modified ions.

Description

technical field [0001] The invention relates to a method for cross-linking modification of medical-grade reconstructed collagen, which belongs to the field of biomedical material preparation. Background technique [0002] Collagen is the basic structural material of vertebrates, the most abundant protein in mammals, and the main protein that constitutes animal connective tissue. It accounts for about 1 / 3 of the total protein in vertebrates, and mainly exists in bones, skin and tendons. Type I collagen, also known as tropocollagen, has a rod-shaped molecule with a length of about 300nm, a diameter of about 1.5nm, and a molecular weight of about 300,000. Its basic structure is a three-strand chain, consisting of two α1(I) and one α2 (1) Chain composition, each α-chain contains 1056 amino acid residues, and the three α-chains are in a right-handed manner, winding each other into three superhelical strands. In fact, all different types of collagen are formed in the form of tri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/24C08L89/00C08K3/32A61L27/24
Inventor 蒋波张焰鲁建魏清荣
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap