Method of manufacturing dampproof flame-proof plaster slab

A gypsum board, refractory technology, applied in the direction of ceramic products, sustainable waste treatment, solid waste management, etc., to achieve the effect of good moisture resistance, mildew resistance and good fire resistance

Active Publication Date: 2011-11-23
北新建材(苏州)有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the moisture-proof and mildew-proof effect of the gypsum board is poor
In addition, although there are moisture-resistant and mildew-resistant gypsum boards on the market, they do not have good fire resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] First take each component (percentage by weight) according to the following proportioning ratio: 0.4% starch, 0.2% glass fiber, 0.04% foaming agent, 0.01% borax, 0.05% paper and 0.1% coagulant, and the remainder is gypsum; , prepared according to the following process:

[0017] a. Break the gypsum first;

[0018] b. Make paper into pulp in the pulp preparation tank, then add borax into the pulp preparation tank and stir with the pulp for 5-10 minutes, then send it into the pulp storage tank and stir for 5-25 minutes, and add borax to the pulp storage tank at the same time Glass fiber stirring for 5 to 25 minutes;

[0019] c. The pulp mixture prepared above, together with additives such as crushed gypsum powder, starch, foaming agent, and coagulant, enter the mixer for stirring, and then go to the forming platform for molding.

Embodiment 2～7

[0021] Prepare according to the components in the following table, and the preparation process is the same as in Example 1.

[0022] Table 1 The proportioning ratio of each component of Examples 2 to 7 (the contents in the table are all weight percentages)

[0023] starch glass fiber Foaming agent Borax Paper coagulant plaster Example 2 0.5 0.2 0.04 0.02 0.05 0.1 margin Example 3 0.6 0.3 0.06 0.03 0.1 0.2 margin Example 4 0.7 0.4 0.07 0.05 0.2 0.3 margin Example 5 0.9 0.5 0.09 0.06 0.3 0.2 margin Example 6 1.0 0.6 0.12 0.07 0.4 0.1 margin Example 7 1.2 0.7 0.15 0.08 0.5 0.3 margin

[0024] The moisture-resistant and fire-resistant paper-faced gypsum boards of the above-mentioned examples 1 to 7 can all meet the following performances: including the upper and lower layers of face paper, the gypsum core ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a moisture-resistant and fire-resistant plasterboard, which comprises the following components (weight percentage): 0.4 to 1.2 percent of starch, 0.2 to 1.0 percent of fibreglass, 0.04 to 0.15 percent of vesicant, 0.01 to 0.08 percent of borax, 0.05 to 0.5 percent of paper and the left plaster. The invention also discloses a moisture-resistant and fire-resistant plasterboard preparation method, which comprises the following steps: a: first pulping paper into a pulp solution, then dissolving the borax into the pulp solution, then adding the fibreglass into the pulp solution to form a pulp mixture; b: mixing and stirring the pulp mixture with mashed land plaster, the starch and the vesicant. The invention not only has good fire-resistant performance, and has good moisture-resistant and rot-resistant performance. In addition, the preparation method also solves associated problem of the borax and the fibreglass in plaster crystal which can not be solved by drying adding boron in the prior art.

Description

technical field [0001] The invention relates to a preparation process of a moisture-resistant and fire-resistant gypsum board. Background technique [0002] Gypsum board is a material made of building gypsum as the main raw material. Because of its light weight, high strength, thinner thickness, convenient processing, and fire resistance, gypsum board is widely used in residential buildings, office buildings, and shops. , Hotels and other places, mainly used as sound-absorbing panels, interior partition walls, ground floor panels, etc. Patent 200410080357.1 discloses a fire-resistant gypsum board, which is mainly composed of gypsum, glass fiber, starch, foaming agent and other raw materials, and has good fire-resistant performance. But this gypsum board has poor moisture resistance and anti-mildew effect. In addition, although there are moisture-resistant and mildew-resistant gypsum boards on the market, they do not have good fire resistance. [0003] Under normal circum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B11/00C04B14/42C04B24/10C04B38/02C04B16/02
CPCC04B2111/0062C04B28/142Y02W30/91C04B14/42C04B18/241C04B22/0013C04B24/38C04B38/02C04B40/0028C04B2103/12
Inventor 王永生郝晓冬
Owner 北新建材(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com