Skin-protection spray for shoes

A technology for sprays and shoes, which is applied to the field of film-coated skin care sprays for shoes, can solve problems such as no occurrence, and achieve the effects of delaying volatilization, avoiding contamination of clothes, and maintaining skin care effects.

Inactive Publication Date: 2009-04-15
金建平
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, skin care products only act on human skin directly in the world. There is no skin care product that is sprayed into the shoe cavity and combined with the fiber structure of the shoe cavity to form a skin care material. The skin of the ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Skin-protection spray for shoes
  • Skin-protection spray for shoes
  • Skin-protection spray for shoes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Composition Weight (%)

[0026] Nano pearl powder 0.5

[0027] Aloe Vera Extract 3

[0028] Silk Peptide Powder 1

[0029] Waterborne polyurethane film former 10

[0030] Silane coupling agent KH-791 0.5

[0031] water 85

[0032] Add 0.5 g of silane coupling agent KH-791 to 85 g of water under magnetic stirring, stir for 5-10 minutes, then add 0.5 g of nano-pearl powder, stir magnetically for 1-2 hours, then add 3 g of aloe extract, 1 gram of silk peptide powder, 10 grams of water-based polyurethane film-forming agent, and then continue to stir for 3 to 4 hours. The prepared emulsion can be made the skin care spray A for shoes of the present invention by the conventional manufacturing process of the spray.

Embodiment 2

[0034] Composition Weight (%)

[0035] Nano pearl powder 1

[0036] Aloe Vera Extract 4

[0037] Silk peptide powder 2

[0038] Waterborne polyurethane film former 20

[0039] Silane coupling agent KH-791 1

[0040] water 72

[0041] Add 1 gram of silane coupling agent KH-791 to 81 grams of water under magnetic stirring, stir for 5 to 10 minutes, then add 1 gram of nano-pearl powder, and after magnetic stirring for 1 to 2 hours, add 4 grams of aloe extract, 2 grams of silk peptide powder, 20 grams of water-based polyurethane film-forming agent, and then continue to stir for 3 to 4 hours. The prepared emulsion can be made the skin care spray B for shoes of the present invention by the conventional manufacturing process of the spray.

Embodiment 3

[0043] Composition Weight (%)

[0044] Nano pearl powder 1.5

[0045] Aloe Vera Extract 5

[0046] Silk Peptide Powder 3

[0047] Waterborne polyurethane film former 30

[0048] Silane coupling agent KH-791 1.5

[0049] water 59

[0050] Add 1.5 grams of silane coupling agent KH-791 to 72.5 grams of water under magnetic stirring, and stir for 5 to 10 minutes, then add 1.5 grams of nano-pearl powder, and after magnetic stirring for 1 to 2 hours, add 5 grams of aloe extract, 3 grams of silk peptide powder, 30 grams of water-based polyurethane film-forming agent, and then continue to stir for 3 to 4 hours. The finished emulsion can be made the skin care spray C for shoes of the present invention by the conventional manufacturing process of the spray.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a skin protection spraying agent used in shoes. The skin protection spraying agent which is sprayed in a shoe cavity can form a layer of film inside the shoe cavity. The layer of film has the functions of moistening and protecting the skin when a user walks with the shoes on. The skin protection spraying agent used in shoes comprises 0.5 to 1.5 weight percent of nanometer pearl powder, 3 to 5 weight percent of aloe extraction solution, 1 to 3 weight percent of silk peptide powder, 10 to 30 weight percent of aqueous polyurethane film former, 0.5 to 1.5 weight percent of silane coupling agent KH-791, and 59 to 85 weight percent of water.

Description

technical field [0001] The invention relates to a coating skin care spray for shoes, in particular to a skin care spray for shoes which is sprayed inside a shoe cavity to moisturize and protect the skin in the shoe cavity. technical background [0002] At present, skin care products only act on human skin directly in the world. There is no skin care product that is sprayed into the shoe cavity and combined with the fiber structure of the shoe cavity to form a skin care material. The skin of the human foot is in contact with the skin care nutrients The skin care effect can also be achieved during the material contact process. Such a skin care spray for shoes has no technical problems, but it has not yet appeared in the field of practical application. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, provide a skin care spray for shoes, spray it in the cavity of the shoe, and form a layer of film inside ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/98A61K8/97A61Q19/00
Inventor 金建平
Owner 金建平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap