Method for processing humid gas curing type vacuum embossing artificial leather

A moisture-curable, processing method technology, applied in the chemical industry, can solve the problems of scratch resistance, thick surface, smooth surface and stiff hand, and achieve the effect of clear texture, bright color and excellent anti-pollution.

Inactive Publication Date: 2009-08-12
无锡市瑞莺合成革有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The artificial leather with deep texture that is common in the market is generally made by hot roller embossing, but the surface of artificial leather made by hot roller embossing is generally not scratch-resistant, and experiments have shown that it can only reach about 100 times at most; while the surface layer is scratch-resistant Generally, the surface of artificial leather is very thick, resulting in smooth surface and stiff hand feeling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The processing method of moisture curing type vacuum embossed artificial leather adopts the following steps

[0013] 1) Artificial leather vacuum embossing: ordinary artificial leather is used as the base embryo and heated to 160-170°C by far-infrared rays, vacuum embossed by a ceramic embossing roller equipped with a vacuum pump, and cooled to room temperature after embossing. The use of far-infrared rays makes the heating process uniform and the energy waste is small, and then passes through the ceramic embossing roller equipped with a vacuum pump. three-dimensional texture.

[0014] 2) Preparation of moisture curing treatment agent: the formula is volume ratio, moisture curing silicone resin LS-3001, 100 parts; toluene TOL, 20 parts; curing agent 7016, 2 parts; defoamer 530, 0.5 parts And leveling agent U-60B, add 0.5 parts into the dye water and stir evenly at high speed. When stirring, use a 32KW high-speed mixer to stir for about one hour, until the dye water and...

Embodiment 2

[0018] The processing method of moisture curing type vacuum embossed artificial leather adopts the following steps

[0019] 1) Artificial leather vacuum embossing: same as Example 1.

[0020] 2) Preparation of moisture curing treatment agent: the formula is volume ratio, moisture curing silicone resin LS-3001, 100 parts; toluene TOL, 30 parts; curing agent 7016, 5 parts; defoamer 530, 1.5 parts And leveling agent U-60B, 1.5 parts; add dye water and stir at a high speed, use a 32KW high-speed mixer to stir for about one hour, until the dye water and moisture-curing resin are fully stirred and then filtered through a 120-mesh nylon filter to Put it in an iron bucket with a plastic sealing bag and let it stand for 1-2 hours until the slurry completely eliminates the air bubbles.

[0021] 3) Moisture curing treatment on the leather surface: same as in Example 1.

[0022] Performance parameters of the finished product in this embodiment: tensile strength greater than or equal to ...

Embodiment 3

[0024] The processing method of moisture curing type vacuum embossed artificial leather adopts the following steps

[0025] 1) Artificial leather vacuum embossing: same as Example 1.

[0026] 2) Preparation of moisture curing treatment agent: the formula is volume ratio, moisture curing silicone resin LS-3001, 100 parts; toluene TOL, 25 parts; curing agent 7016, 3 parts; defoamer 530, 15 parts And leveling agent U-60B, 1 part; add dye water and stir evenly at high speed, use a 32KW high-speed mixer to stir for about one hour when stirring, until the dye water and moisture curing resin are fully stirred evenly, then filter through a 120-mesh nylon filter to Put it in an iron bucket with a plastic sealing bag and let it stand for 1-2 hours until the slurry completely eliminates the air bubbles.

[0027] 3) Moisture curing treatment on the leather surface: same as in Example 1.

[0028] Performance parameters of the finished product in this example: tensile strength greater tha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for processing moisture cured vacuum embossed artificial leather, which comprises the following steps that: common artificial leather is taken as a base and heated by far infrared rays to be between 160 and 170 DEG C; and a ceramic embossing roller provided with a vacuum pump is used for vacuum embossing, and the common artificial leather is cooled to normal temperature, undergoes moisture curing posttreatment, and is stood for more than 24 hours to form a finished product. When passing a heating roller, the artificial leather is tightly absorbed onto the surface of the ceramic roller by the pull of vacuum in the roller, and then generates grains with strong third dimension; and the surface of the product has very high physical scratch resistance which exceeds 1,000 times in back-and-forth friction scratch resisting tests through experiments, and has the rebound elasticity, super smooth handfeel, anti-fouling and excellent hydrolytic resistance.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to a processing method of moisture curing type vacuum embossed artificial leather. Background technique [0002] With the continuous progress of the development of artificial leather, people have higher and higher requirements for the three-dimensional effect of the artificial leather grain and the physical and chemical properties of the leather surface layer, which has led to a lot of efforts in the leather manufacturing process to meet the market demand in these two aspects. The artificial leather with deep texture that is common in the market is generally made by hot roller embossing, but the surface of the artificial leather made by hot roller embossing is generally not scratch-resistant, and experiments have shown that it can only reach about 100 times at most; while the surface layer is scratch-resistant Types of artificial leather generally have a thick surface, r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P5/24D06M15/643
Inventor 宗政宇叶均
Owner 无锡市瑞莺合成革有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com