Environment-friendly composite polishing wax and production method thereof
A composite polishing, environmentally friendly technology, applied in polishing compositions, chemical instruments and methods, polishing compositions containing abrasives, etc., to achieve the effects of good stability, easy application and high finish
Inactive Publication Date: 2012-02-22
吴壮城
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The purpose of the present invention is to overcome the shortcomings of the existing solvent-based polishing agent, to provide an environmentally friendly and efficient composite polishing wax and its production method
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0008] Put 1.7kg of paraffin wax and 7.0kg of stearic acid into an enamel vessel, heat to 90-120°C, after the paraffin wax and stearic acid are completely melted, add 1.0kg of chromium oxide polishing powder, the particle size of chromium oxide polishing powder is: 0.5 μm~7μm, stir evenly, then add 0.3kg lanolin, keep warm for 120 minutes under stirring state, carry out chemical modification compound reaction, after the reaction, the grout is discharged into the prefabricated mold, the mold is introduced into the water tank to cool, and it becomes a block after solidification product.
[0009] The main technical parameters of the environmentally friendly and efficient composite polishing wax are:
[0010] pH value: 8-10;
[0011] Curing point: 50-60°C;
[0012] Cleaning power: artificial oil ≥ 90%;
[0013] Corrosion performance: 45# steel grade 0;
[0014] Gloss: 38-80 degrees;
[0015] Cutting force: 0.008-0.02N.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to an environment-friendly and high-efficiency composite polishing wax for polishing metal or non-metal surfaces and a production method thereof. The ingredients of the composite polishing wax include the following raw materials in weight ratio: stearic acid 65-75; chromium oxide polishing powder 8-12; paraffin wax 10-25; lanolin 2-3.5. The method is to put the formula amount of paraffin and stearic acid into the enamel vessel, heat it to 90-120°C, after the paraffin melts, add chromium oxide polishing powder, stir evenly, and then add lanolin at 110±5 The chemical modification compound reaction is carried out under the condition of ℃, and the reaction time is 2±0.5h. After the reaction, the grout flows into the prefabricated mold, and the mold is introduced into the water tank to cool, and it becomes a block product after solidification. The product does not contain harmful solvents, is safe and convenient to make, saves energy consumption, has no environmental pollution, and is suitable for various polishing methods.
Description
Technical field: [0001] The invention relates to an environment-friendly and high-efficiency composite polishing wax for polishing metal or non-metal surfaces and a production method thereof. Background technique: [0002] Existing polishing agents (pastes) for metal or non-metal surfaces are mainly composed of paraffin, abrasives, solvents and additives, but solvent-based polishing agents have disadvantages such as unstable product quality and environmental pollution. Invention content: [0003] The object of the present invention is to overcome the shortcomings of the existing solvent-based polishing agents, and provide an environmentally friendly and efficient composite polishing wax and a production method thereof. [0004] The composite polishing wax of the present invention comprises the following raw materials in weight ratio: stearic acid 65-75; chromium oxide polishing powder 8-12; paraffin wax 10-25; lanolin 2-3.5. [0005] The method for producing the environme...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/08C09G1/02
Inventor 吴壮城吴承斌吴启斌
Owner 吴壮城