Method of producing polyester amide hot melt adhesive

A technology of polyester amide and its manufacturing method, which is applied in the direction of adhesives, etc., can solve the problems of uncontrollable relative content and sequence distribution of ester bond and amide bond, uncertain melting range and proportion of polyester glue and polyamide glue, etc., to achieve Plump appearance quality, not easy to store, excellent dry cleaning resistance

Inactive Publication Date: 2009-11-25
陈国新
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a polyester amide hot-melt adhesive manufacturing method, which can effectively solve the problem that the relative content and sequence distri

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of producing polyester amide hot melt adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] refer to figure 1 An embodiment of the method for producing polyester amide hot-melt adhesive of the present invention, the polyester adhesive with a melting range of 130-140°C and the polyamide adhesive with a melting range of 140-150°C are added to the reactor at a weight ratio of 1:1. Then add polyester glue and polyamide glue total weight 0.1% acetate catalyst and 0.01% phosphite antioxidant. Under the protection of nitrogen, slowly heat until the colloidal particles melt, start stirring, raise the temperature to 240-250°C and maintain for 3-4 hours to carry out chain exchange reaction. Then slowly depressurize until the melt viscosity reaches 77.3Pa·s, remove the low molecular matter in the reaction system, and when the melt viscosity reaches the requirement, fill nitrogen to normal pressure and then change to 1.08 atmospheric pressure, and press the melt material in a strip shape Put it into a water tank, cool, and cut into pellets to obtain colloidal pellets.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method of producing polyester amide hot melt adhesive, comprising the steps as follows: adding the polyester adhesive with melting range being 130 to 140 DEG. C and polyamide adhesive being 140 to 150 DEG. C into a reaction kettle according to 1:1 weight ratio, then adding catalyst and antioxidant into the reaction kettle, slowly heating until the colloid melting under the protection of nitrogen, stirring, heating to carry out chain exchange reaction, then slowly decompressing until the melt viscosity being 72.3 to 78.3 Pa.s, filling the nitrogen to the normal pressure, then changing to 1.03 to 1.09 high atmospheric pressure to obtain melt material, pressing the melt material into sink by strip shape, cooling, cutting to obtain colloid. The invention has the advantages of effectively controlling the contents and sequence distribution of ester linkage and amido link of the colloid, solving the shortcomings that the daiamid has large dependence to the temperature, and the adhesive is easy to percolate from liner, and the absorption ratio is high and is difficult to store, and is easy to discolor under illumination.

Description

technical field [0001] The invention relates to a method for manufacturing hot-melt adhesives, in particular to a method for manufacturing polyester amide hot-melt adhesives. Background technique [0002] Polyester hot melt adhesive has high heat resistance, good weather resistance, water wash resistance and elasticity, but it is not suitable for fabric hot melt adhesive due to its high melting point, high viscosity when heated and melted, and poor dry cleaning resistance. ; Polyamide hot-melt adhesive has excellent flexibility, good aging resistance and dry cleaning resistance, low melting temperature, and is convenient for garment processing operations, but its washing resistance is poor. [0003] Polyester amide hot melt adhesive is made by mixing polyester glue and polyamide glue to obtain colloidal particles. Since polyester amide products are co-condensed with both ester bonds and amide bonds on a macromolecular chain The relative content and sequence distribution of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J177/12
Inventor 严惠莲
Owner 陈国新
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap