Method for welding aluminum materials

A welding method and technology of aluminum materials, which are applied in the field of welding, can solve the problems of insufficient welding fastness and shallow welding depth, etc., and achieve the effects of increasing welding fastness, increasing depth, and strengthening fastness

Active Publication Date: 2010-02-17
KONFOONG MATERIALS INTERNATIONAL CO LTD
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The problem solved by the invention is that the existing welding depth is shallow and the welding fastness is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for welding aluminum materials
  • Method for welding aluminum materials
  • Method for welding aluminum materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In step S101 , the first welding portion 13A is formed on the first aluminum tube 1A by machining, and the second welding portion 23A is formed on the second aluminum tube 2A.

[0032] In this embodiment, the prior art such as Figure 1A In the shown aluminum tube, the first aluminum tube 1A has a first tube wall 11A, and the cross section of the first tube wall 11A is circular. Wherein, the first pipe wall 11A has a first joint area 16A, and the first joint area 16A has a first welding surface 12A. The second aluminum tube 2A has a second tube wall 21A, and the cross section of the second tube wall 21A is circular. Wherein, the second pipe wall 21A has a second joint area 26A, and the second joint area 26A has a second welding surface 22A.

[0033] Then, the first welding portion 13A is formed on the first joining region 16A of the first aluminum tube 1A by machining. Form the second welding portion 23A on the second joint area 26A of the second aluminum pipe 2A, suc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for welding aluminum materials, comprising the following steps: forming a first welding part on a first bonding area of a first aluminum material and forming a secondwelding part on a second bonding area of a second aluminum material; splicing the first welding part and the second welding part to form a welding groove; and performing welding at the welding grooveby using a spray gun, forming a molten pool due to the entrance of solders into the welding groove during heating, and finally forming welding points after the molten pool is cooled. The welding points formed by the method have high depth, thereby enhancing the firmness of welding.

Description

technical field [0001] The invention relates to a welding method, in particular to an inert gas shielded welding method for aluminum materials. Background technique [0002] Aluminum materials are easily oxidized during welding to form alumina, which has a high melting point and is very stable, thereby hindering the melting and fusion of the base metal. At present, inert gas shielded welding is mostly used for welding aluminum and aluminum alloys, which can prevent the oxidation of aluminum during welding. Inert gas shielded welding includes non-melting extremely inert gas shielded welding and melting extremely inert gas shielded welding. [0003] Non-melting pole inert gas shielded welding is that the arc burns between the non-melting pole and the workpiece, and an inert gas that does not chemically react with the metal flows around the welding arc to form a protective gas cover, so that the non-melting pole, arc and The molten pool and the metal already at high temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K9/235B23K9/16
Inventor 姚力军潘杰王学泽汪涛刘庆
Owner KONFOONG MATERIALS INTERNATIONAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com