Carboxymethyl chitosan/polyvinyl alcohol compound sponge and preparation method thereof
A technology of carboxymethyl chitosan and polyvinyl alcohol, used in medical science, absorbent pads, prostheses, etc., to achieve the effects of good elasticity, good biocompatibility and high water absorption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] Add polyvinyl alcohol and carboxymethyl chitosan according to the percentage by weight of each raw material: 23% polyvinyl alcohol and 10% carboxymethyl chitosan, add them to a three-necked bottle, reflux and dissolve at 90°C for 30 minutes, Pour the solution into a beaker and add 33% sulfuric acid, 26% formaldehyde and 8% foaming agent. After fully mechanically stirring, the blend is poured into a mold, and thermoformed in an oven at 50°C for 4 hours to obtain a composite sponge sample ( A carboxymethyl chitosan / polyvinyl alcohol composite sponge material).
Embodiment 2
[0021] Add polyvinyl alcohol and carboxymethyl chitosan according to the percentage by weight of each raw material: 25% polyvinyl alcohol and 15% carboxymethyl chitosan are added to a three-necked bottle, and after condensing and refluxing at 90°C for 35 minutes, the Pour the solution into a beaker and add 29% of sulfuric acid, 24% of formaldehyde and 7% of foaming agent. After fully mechanically stirring, the blend is poured into a mold, and thermoformed in an oven at 60°C for 6 hours to obtain a composite sponge sample (one A carboxymethyl chitosan / polyvinyl alcohol composite sponge material).
Embodiment 3
[0023] Add polyvinyl alcohol and carboxymethyl chitosan according to the percentage by weight of each raw material: 26% polyvinyl alcohol and 13% carboxymethyl chitosan are added to a three-necked bottle, and after condensing and refluxing at 90°C for 40 minutes, the Pour the solution into a beaker and add 28% hydrochloric acid, 25% formaldehyde and 8% foaming agent. After fully mechanically stirring, the blend is poured into a mold, and thermoformed in an oven at 60°C for 8 hours to obtain a composite sponge sample (one A carboxymethyl chitosan / polyvinyl alcohol composite sponge material).
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap