Preparation method of binding agent applied to environment-friendly aluminum structure composite material

A composite material and environment-friendly technology, applied in adhesive types, polyether adhesives, polyurea/polyurethane adhesives, etc., can solve the problems of irritating gas volatilization, high cost, poor applicability, etc. Achieve high composite fastness, excellent weather resistance and excellent applicability

Inactive Publication Date: 2010-06-09
NANTONG GAOMENG NEW MATERIAL
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are problems with adhesives for composite materials, mainly because the environmental performance and impact strength of the composite materials obtained after bonding are poor. Due t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] This embodiment 1 provides a method for preparing an adhesive for environmentally friendly aluminum structure composite materials. The prepared adhesive has excellent composite performance and stable operation performance, and is suitable for various aluminum substrates to prepare environmentally friendly composite materials. The preparation method specifically includes:

[0018] Preparation of polyester polyester:

[0019] a. Esterification:

[0020] 10-20 parts by mass of dimethyl terephthalate, 25-35 parts by mass of ethylene glycol, 20-40 parts by mass of adipic acid, and 25-35 parts by mass of 1,4-butanediol are added to the poly In the ester synthesis kettle, heat up to 210-240°C, react for 6-8 hours, and the esterification is completed; in this esterification step, keep the distillate of the distillate from the polyester synthesis kettle stable at 1-3 parts by mass / Hours; after the esterification reaction is completed, take a sample to measure the acid value t...

Embodiment 2

[0031] This embodiment 2 provides a method for preparing an adhesive for an environmentally friendly aluminum structure composite material. The prepared adhesive can be used for compounding various aluminum substrates to prepare an environmentally friendly composite material. The preparation method specifically includes:

[0032] (1) Preparation of polyester polyol:

[0033] Get each raw material according to the following ratio:

[0034] Raw material ratio (parts by mass)

[0035] Dimethyl terephthalate 15

[0036] Ethylene glycol 20

[0037] Adipic acid 40

[0038] 1,4 Butanediol 25

[0039] Preparation of polyester polyol:

[0040] a. Esterification:

[0041] The dimethyl terephthalate of 15 mass parts, the ethylene glycol of 20 mass parts, the adipic acid of 40 mass parts, the 1,4 butanediol of 25 mass parts join in the polyester synthesis kettle, be heated up to 220 ℃, react for 8 hours, and complete the esterification; during the esterification process, pay attent...

Embodiment 3

[0058] This embodiment three provides a method for preparing an adhesive for an environmentally friendly aluminum structure composite material. The prepared adhesive can be used for compounding various aluminum substrates to prepare an environmentally friendly composite material. The preparation method specifically includes:

[0059] (1) Preparation of polyester polyol:

[0060] Get each raw material by following mass ratio:

[0061] Raw material ratio (parts by mass)

[0062] Dimethyl terephthalate 20

[0063] Ethylene glycol 30

[0064] Adipic acid 25

[0065] 1,4 Butanediol 25

[0066] The method for preparing polyester polyol in this example is basically the same as the method for preparing polyester polyol given in Example 2, see Example 2, and will not be repeated here. The esterification step reaction of preparing polyester polyol is completed, and the acid value of the sampled product is measured to be 15mgKOH / g (≤25mgKOH / g), indicating that the esterification ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Oil absorption valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a binding agent applied to an environment-friendly aluminum structure composite material and belongs to the field of binding agent preparation.The method comprises the following steps: esterifying dimethyl terephthalate, ethylene glycol, hexanedioic acid, 1,4 butanediol under certain conditions, then carrying out condensation polymerization on the raw materials to obtain polyester polyol; mixing the obtained polyester polyol with polyether glycol, then formulating the mixture by inorganic filler, tackified resin and organosilicon coupling agent according to proportion, thus obtaining an environment-friendly aluminum structure composite material compound binding agent.In the preparation method, through the design of the structure of polyesterchain segment, introduction of polyether glycol chain segment unit and adjustment of proportioning of different inorganic fillers, the prepared binding agent is endowed with extremely high aluminum base material strength and fine operability; in addition, with the binding agent adopted, various compound materials containing aluminum base materials can be produced.The aluminum honeycomb compound product made from the binding agent of the invention features high mechanical property, no discharge of toxic and irritant gas and excellent weather resistance.

Description

technical field [0001] The invention relates to the field of preparation of adhesives, in particular to a method for preparing adhesives for environment-friendly aluminum structure composite materials. Background technique [0002] Currently, aluminum-containing substrates are bonded together by aluminum structural adhesives, making it a new class of composite materials with unique properties and low cost. A typical product of this composite material is an aluminum honeycomb panel, which has the advantages of light weight and less than 1 / 3 of the weight of an aluminum veneer. Because the aluminum honeycomb panel has the advantages of good toughness and high strength, it can be designed for heavy panels, cheap to maintain, and has good sound insulation and heat insulation performance. This aluminum honeycomb composite material is mainly used in the construction and decoration industries, and has excellent properties such as high wind pressure resistance, shock absorption, so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J171/02C09J167/02C09J175/08C09J175/06
Inventor 冯祎沈峰
Owner NANTONG GAOMENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products