Preparation method of binding agent applied to environment-friendly aluminum structure composite material
A composite material, environmentally friendly technology, applied in the direction of adhesive types, polyether adhesives, polyurea/polyurethane adhesives, etc., can solve the problems of irritating gas volatilization, poor applicability, high cost, and achieve The effect of high compound fastness, excellent applicability and excellent weather resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] The first embodiment provides a method for preparing an adhesive for an environment-friendly aluminum structure composite material. The prepared adhesive has excellent compounding properties and stable operation performance, and is suitable for compounding various aluminum substrates to prepare an environment-friendly compound material. The preparation method specifically includes:
[0018] To prepare polyester polyester:
[0019] a. Esterification:
[0020] 10-20 parts by mass of dimethyl terephthalate, 25-35 parts by mass of ethylene glycol, 20-40 parts by mass of adipic acid, and 25-35 parts by mass of 1,4-butanediol are added to the polymer. In the ester synthesis kettle, the temperature is raised to 210 to 240° C., and the reaction is performed for 6 to 8 hours, and the esterification is completed; in this esterification step, the distillate of the polyester synthesis kettle is kept stable at 1 to 3 parts by mass / After the esterification reaction is completed, s...
Embodiment 2
[0031] The second embodiment provides a method for preparing an adhesive for an environmentally friendly aluminum structure composite material. The prepared adhesive can be used for compounding various aluminum substrates to prepare an environmentally friendly composite material. The preparation method specifically includes:
[0032] (1) Preparation of polyester polyol:
[0033] Take each raw material according to the following proportions:
[0034] Raw material ratio (mass parts)
[0035] Dimethyl terephthalate 15
[0036] Glycol 20
[0037] Adipic acid 40
[0038] 1,4 Butanediol 25
[0039] To prepare polyester polyols:
[0040] a. Esterification:
[0041] 15 parts by mass of dimethyl terephthalate, 20 parts by mass of ethylene glycol, 40 parts by mass of adipic acid, and 25 parts by mass of 1,4 butanediol were added to the polyester synthesis kettle, and the temperature was raised to 220 ℃, react for 8 hours to complete the esterification; during the esterification p...
Embodiment 3
[0058] The third embodiment provides a preparation method of an adhesive for an environmentally friendly aluminum structure composite material. The prepared adhesive can be used for compounding various aluminum substrates to prepare an environmentally friendly composite material. The preparation method specifically includes:
[0059] (1) Preparation of polyester polyol:
[0060] Take the raw materials according to the following mass ratios:
[0061] Raw material ratio (mass parts)
[0062] Dimethyl terephthalate 20
[0063] Glycol 30
[0064] Adipic acid 25
[0065] 1,4 Butanediol 25
[0066] The method for preparing the polyester polyol in this embodiment is basically the same as the method for preparing the polyester polyol given in the second embodiment, and reference may be made to the second embodiment, which will not be repeated here. The esterification step for preparing polyester polyol is completed, and the acid value of the sampled product is measured to be 15 m...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
acid value | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap