Waterborne lotus leaf paint

A lotus leaf paint, water-based technology, applied in the field of wall paint, can solve the problems of anti-fouling, poor water and alkali resistance, aging resistance, poor anti-mildew and anti-algae functions, and high surface tension of the paint film, so as to improve the product quality. Stability, improve the hydrophobicity of the paint film, improve the effect of dispersion stability and water resistance

Active Publication Date: 2012-07-04
广东黑马新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, many wall paints cannot solve these problems or cannot completely solve these problems. The membrane has high surface tension, strong hydrophilicity, and is not safe and environmentally friendly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Equip 100kg lotus leaf paint of the present invention, it is formulated by the raw material of following weight content:

[0028] 17.25kg of clean tap water, 0.5kg of polycarboxylate amine salt, 0.1kg of polyoxyethylene ether, 0.2kg of pH regulator, 0.35kg of a mixture of silicone and mineral oil, 3kg of ethylene glycol, and 3.5kg of tripropylene glycol butyl ether, 5kg of pure silicone polymer, 21kg of rutile titanium dioxide, 5kg of talcum powder, 43kg of styrene-acrylic emulsion, 0.35kg of polyurethane thickener, 0.6kg of antifungal agent, and 0.15kg of isothiazolinone .

[0029] Feed according to the conventional paint-making process sequence, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform, and the water-based lotus leaf paint of the present invention is obtained.

Embodiment 2

[0031] Equip 100kg lotus leaf paint of the present invention, it is formulated by the raw material of following weight content:

[0032] 16.4kg of clean tap water, 0.8kg of polycarboxylate amine salt, 0.15kg of polyoxyethylene ether, 0.1kg of pH regulator, 0.4kg of a mixture of silicone and mineral oil, 3.5kg of ethylene glycol, and 4.0kg of tripropylene glycol butyl ether , 6kg of pure silicone polymer, 19kg of rutile titanium dioxide, 4kg of talcum powder, 45kg of styrene-acrylic emulsion, 0.15kg of polyurethane thickener, 0.3kg of antifungal agent, and 0.2kg of isothiazolinone .

[0033] Feed according to the conventional paint-making process sequence, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform, and the water-based lotus leaf paint of the present invention is obtained.

Embodiment 3

[0035] Equip 100kg lotus leaf paint of the present invention, it is formulated by the raw material of following weight content:

[0036] 17.65kg of clean tap water, 0.6kg of polycarboxylate amine salt, 0.2kg of polyoxyethylene ether, 0.1kg of pH regulator, 0.7kg of a mixture of silicone and mineral oil, 2.5kg of ethylene glycol, and 4.3kg of tripropylene glycol butyl ether , 8kg of pure silicone polymer, 18kg of rutile titanium dioxide, 7.5kg of talcum powder, 40kg of styrene-acrylic emulsion, 0.25kg of polyurethane thickener, 0.5kg of antifungal agent, and 0.5kg of isothiazolinone 0.2kg.

[0037] Feed according to the conventional paint-making process sequence, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform, and the water-based lotus leaf paint of the present invention is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne lotus leaf paint, which contains the following materials by weight percent: 10-30 percent of clean tap water, 0.5-1.3 percent of polycarboxylic acid ammonium salt, 0.05-0.4 percent of surfactant, 0.1-0.3 percent of PH regulator, 0.4-0.8 percent of defoamer, 1.5-4 percent of ethylene glycol, 1.0-5.0 percent of film forming assistant, 10-30 percent of titanium white, 5-15 percent of talcum powder, 3-10 percent of organosilicon, 25-55 percent of emulsion, 0.1-0.8 percent of thickener, 0.1-1.0 percent of mildew preventive and 0.1-0.5 percent of preservative. The invention overcomes the defects in the prior art and has the advantages of simple construction, good recoatability, good water-fast alkali resistance, good mildew and algae prevention capacity, strong adhesive force, good weather resistance and strong hydrophobicity.

Description

technical field [0001] The invention relates to a wall paint, in particular to a water-based lotus leaf paint. Background technique [0002] In wall construction, problems such as strong hydrophilicity of the paint film, poor stain resistance, wall cracking, blooming, powdering, peeling, mildew, and poor recoatability have long plagued people's home life and urban beauty. These can be solved by brushing the wall paint. Wall paint is a colloidal solution. Apply it on the surface of the object, and after a period of physical and chemical changes, it will form a tough and continuous film firmly bonded to the surface of the coated object to realize its protective function, decorative function and other special functions. At present, many wall paints cannot solve these problems or cannot completely solve these problems. The membrane has high surface tension, strong hydrophilicity, and is not safe and environmentally friendly. Contents of the invention [0003] The purpose o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D5/28C09D5/33C09D183/00
Inventor 黄宏亭
Owner 广东黑马新材料科技有限公司