Method for producing low-temperature impact resistance high-strength nodular cast iron

A low-temperature impact-resistant, nodular cast iron technology is applied in the direction of improving process efficiency and can solve problems such as insufficient strength

Active Publication Date: 2010-06-30
山东汇金股份有限公司
View PDF1 Cites 56 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the grade QT450-10 ductile iron, in terms of low temperature impact toughness performance, its strength cannot meet the requirements of low temperature application at low temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing low-temperature impact resistance high-strength nodular cast iron
  • Method for producing low-temperature impact resistance high-strength nodular cast iron
  • Method for producing low-temperature impact resistance high-strength nodular cast iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0038] 1. Raw material preparation

[0039] 1. Raw iron: High-purity pig iron purchased from Shanxi Province is used.

[0040] 2. Scrap steel: High-quality medium and low-carbon scrap steel must be derusted before use.

[0041] 3. Nodulizer: Low Re and low Mg alloy produced by Nanjing Pujiang Alloy Factory.

[0042] 4. Inoculant: Silicon-barium alloy produced by Qufu Foundry Material Factory is used for inoculation in the bag.

[0043] 5. Desulfurizer: The deep desulfurizer produced by Yantai Shenglida Company is used.

[0044] 6. Carburizer, covering agent and slag collecting agent adopt existing materials.

[0045] 2. Material requirements: grade QT450-10.

[0046] 3. The achieved chemical composition ω (%):

[0047] C 3.5~3.9%, Si 1.8%~2.5%, Mn≤0.2%, P≤0.05%, S≤0.015%, Mg0.03~0.06%, Re 0.01~0.03%, Ti≤0.055%, Cu 0.15- 0.50%, the balance is Te.

[0048] Fourth, the achieved mechanical properties:

[0049] бb≥450Mpa, σ0.2≥310Mpa, δ≥10%, Akv value at -20°C±2°C: average ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing low-temperature impact resistance high-strength nodular cast iron, which comprises processes of material preparing, smelting, desulfurizing, molten iron adjusting and spheroidizing. The method is characterized in that: in the material preparing process, based on 100 percent, base iron accounts for 30 to 70 percent, steel scarp accounts for 10 to 20 percent, and recirculated iron accounts for 10 to 60 percent; other additives are added based on the total weight of the base iron, the steel scarp and the recirculated iron, wherein spheroidizing agent accounts for 1.6 to 2.0 percent, inoculant accounts for 0.4 to 0.6 percent, desulfurizer accounts for 1.2 to 1.8 percent, and carburant accounts for 1 to 3 percent; furthermore, 0.15 to 0.50 percent of Cu is added. On the premise of ensuring low temperature impact performance, the nodular cast iron improves strength,, meets the requirement that the nodular cast iron of the mark has higher low-temperature impact resistance and high normal-temperature strength, and can be widely used for manufacturing important high-strength cast of vehicles, locomotive, draught fans and engineering machinery used in low temperature environment and manufacture of cast having strict requirement on fatigue strength.

Description

technical field [0001] The invention relates to a production method of nodular cast iron, which belongs to iron-carbon alloy, in particular to a production method of low-temperature impact-resistant high-strength nodular cast iron. It is mainly suitable for the manufacture of important high-strength parts of automobiles and construction machinery used in low-temperature environments. Background technique [0002] Ductile iron mainly exists in the form of spherical graphite by using magnesium or magnesium alloy as a nodularizing agent. At present, nodular cast iron has been widely used. However, due to different application fields, the requirements for its performance are also different, and its production methods are also different. At present, my country's standards only specify the impact value and low-temperature impact value requirements for grades QT400-18 and QT400-18L ductile iron (as shown in Table 1), but for the material of grade QT450-10 ductile iron, due to rel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/08B22D1/00C21C7/064C22C37/10
CPCY02P10/20
Inventor 张杰陈淦张务才
Owner 山东汇金股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap