A kind of manufacturing method of aluminum, stainless steel composite metal strip

A clad metal plate and manufacturing method technology, applied in metal rolling, roll speed control, tension/pressure control and other directions, can solve the problem of inability to obtain aluminum and stainless steel clad metal plates and strips, difficult to solve problems of aluminum oxidation, and unstable product quality and other problems, to achieve significant economic effects, solve oxidation problems, and stabilize product quality.

Active Publication Date: 2012-02-22
LUOYANG TONGYI METAL MATERIAL DEV +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current production method has disadvantages such as high cost, low efficiency, low composite strength, and unstable product quality, especially when aluminum is composited with stainless steel, the oxidation problem of aluminum is difficult to solve, and the current production method can only produce a single plate , can not get continuous aluminum and stainless steel clad metal strip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A method for manufacturing aluminum and stainless steel composite metal strips, comprising the following steps: heating and smelting metal aluminum, refining and degassing at 800°C, and after refining and degassing, when the temperature of the aluminum liquid is 690°C, the molten aluminum is Stand still for 5 minutes, and then pour into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; select a stainless steel strip with a thickness of 0.1mm, and the stainless steel strip is first treated with alkali washing and degreasing , and then put the stainless steel strip close to the surface of the grinding roller for single-sided online grinding until there is no oxide layer on the surface. After grinding, the stainless steel strip is heated online to 150°C; the semi-solid aluminum and stainless steel strip Grinding surface contact, anaerobic continuous casting and rolling, the rolling ...

Embodiment 2

[0014] A method for manufacturing aluminum and stainless steel composite metal strips, comprising the following steps: heating and melting the aluminum alloy liquid according to the chemical composition of the aluminum alloy grade 1050, refining and degassing at 790°C, and after the refining and degassing, when the aluminum liquid When the temperature is 750°C, let the liquid aluminum stand still for 10 minutes, and then pour it into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; Strip, two stainless steel strips are treated with alkali washing and degreasing respectively, and then the two stainless steel strips are respectively attached to the roller surface of the upper and lower grinding rollers for single-sided online grinding until there is no oxide layer. After grinding, the stainless steel The strip is heated online to 220°C; semi-solid aluminum is brought into contact with th...

Embodiment 3

[0016] A method for manufacturing aluminum and stainless steel composite metal strips, comprising the following steps: heating and melting aluminum alloy liquid according to the chemical composition of aluminum alloy grade 1070, refining and degassing at 810°C, and after refining and degassing, when the aluminum liquid When the temperature is 820°C, let the molten aluminum stand for 10 minutes, and then pour it into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; two stainless steel plates with a thickness of 2mm are selected. The two stainless steel strips are respectively treated with alkali washing and degreasing, and then the two stainless steel strips are respectively attached to the roller surfaces of the upper and lower grinding rollers for single-sided online grinding until there is no oxide layer. After grinding, the stainless steel plates are The strip is heated to 200°C on-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing aluminum and stainless steel composite metal strips. In the method, semi-solid aluminum or aluminum alloy and solid stainless steel strips are subjected to anaerobic continuous casting and rolling to obtain aluminum and stainless steel composite metal strips. In the manufacturing method of the present invention, solid stainless steel strips and molten aluminum realize non-oxidative metallurgical compounding, which solves the problem of aluminum oxidation, and the composite strength is high, and the bonding strength of stainless steel and aluminum is ≥ 100 MPa; continuous casting and rolling of stainless steel strips and molten aluminum The production efficiency of aluminum and stainless steel composite metal strips is greatly improved, which can be increased by dozens of times, and the product quality is stable; the produced aluminum and stainless steel composite metal strips maintain the original surface quality of stainless steel strips, and the thickness of the stainless steel layer It is uniform and can be cold-rolled and deep-processed; various stainless steel strips and aluminum liquids with different components can be used, and there are many types of products and wide applicability; the production technology of the present invention is advanced, the number of processes is small, energy-saving, material-saving, and economical effects are remarkable.

Description

technical field [0001] The invention relates to the technical field of manufacturing metal strips, in particular to a method for manufacturing aluminum and stainless steel composite metal strips. Background technique [0002] Stainless steel and aluminum are important metals widely used in industrial and civil fields. Stainless steel will not cause corrosion, pitting, rust or wear. Stainless steel is also one of the strongest materials among metal materials used in construction. Due to its good corrosion resistance, stainless steel can make structural components permanently maintain the integrity of engineering design . Chromium-containing stainless steel also combines mechanical strength and high elongation, and is easy to process and manufacture parts, which can meet the needs of architects and structural designers. Aluminum has a small specific gravity, good electrical and thermal conductivity, and aluminum resources are abundant and cheap. [0003] Aluminum and stainl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/38B21B37/46B21B37/48
Inventor 尚郑平符会文叶晋予尚爱平符利强刘向伟王晓雨谢敬佩王文焱王爱琴李继文李洛利
Owner LUOYANG TONGYI METAL MATERIAL DEV