Fiber opening process of electronic grade glass fiber cloth and size used in same

A technology of electronic cloth and slurry, which is applied in fiber processing, textiles and paper making, and can solve problems such as poor appearance of hairiness and broken threads on the cloth surface

Active Publication Date: 2010-08-11
SHANGHAI GRACE FABRIC
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention uses the chemical fiber opening method to avoid the defects of poor appearance such as broken threads on the cloth surface and hairiness caused by excessive physical fiber opening in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber opening process of electronic grade glass fiber cloth and size used in same
  • Fiber opening process of electronic grade glass fiber cloth and size used in same
  • Fiber opening process of electronic grade glass fiber cloth and size used in same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] Below in conjunction with the accompanying drawings, the embodiments of the present invention are described in detail: the present embodiment is implemented on the premise of the technical solution of the present invention, and provides detailed embodiments and specific operation processes, but the protection scope of the present invention is not limited to the following described embodiment.

[0033] Table 1-1 Slurry formula table (each component by mass percentage)

[0034]

Slurry formula

implement

Example 1-1

implement

Example 2-1

implement

Example 3-1

implement

Example 4-1

implement

Example 5-1

implement

Example 6-1

implement

Example 7-1

implement

Example 8-1

Compare

Example 0-1

The amount of leavening agent added

0.05%

0.1%

0.5%

0.7%

0.8%

1.0%

1.5%

2.0%

0

2116 main slurry

PVA ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fiber opening process of electronic grade glass fiber cloth and size used in the same. The fiber opening process is applied to the technical field of electronic grade glass fibers and is characterized by preparing and boiling the size: in particular, firstly weighing a certain amount of main size PVA and then pouring the PVA into a size boiling barrel, adding a certain amount of deionized water, stirring the mixture and raising the temperature to dissolve the PVA, then adding the weighed leavening agent after the PVA is completely dissolved and becomes transparent and clear solution, and preserving heat for half an hour after stirring the mixture until the PVA is completely dissolved, thus the size can be used. The size comprises the following components in percentage by mass: 5-10% of main size PVA, 0.5-1% of added leavening agent and the balance water. The invention provides the fiber opening technology of the electronic grade glass fiber cloth suitable for printed-circuit boards with high precision, high uniformity and high performance. The electronic grade glass fiber cloth prepared by the fiber opening technology is thin and uniform, has faster resin impregnation, is suitable for the insulation enhanced materials of the printed-circuit boards and is extensively applied to the high-end products such as mobile phone boards, notebook computers, automotive sheets, digital cameras, digital players, navigation equipment and the like.

Description

technical field [0001] The invention relates to a process applied in the technical field of electronic-grade glass fiber cloth weaving and its slurry, in particular to a fiber-opening process of electronic-grade glass fiber cloth and its slurry. Background technique [0002] The glass fiber yarn used as electronic-grade glass fiber cloth is an alkali-free glass fiber (E-glass) whose main component is SiO 2 , Al 2 O 3 , CaO ternary system, on this basis, add B 2 O 3 Replace part of SiO 2 , MgO replaces part of CaO to form the current general alkali-free glass fiber, and its main raw materials are silica sand, limestone, boron oxide, etc. The glass fiber yarn manufacturing process is to pulverize the raw ores, disperse them evenly, mix and melt them in a furnace at about 1300 °C, and use the gravity to make the high-temperature glass liquid through the spinning box to be rapidly unloaded and extracted into silk. The diameter of a single fiber is Between 4-9μm, then tens ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/333D06M13/467
Inventor 毛嘉明杜甫严海林邹新娥孙小虎徐璟王传江刘晨
Owner SHANGHAI GRACE FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products