Novel fireproof module and manufacturing method thereof

A new type of fire resistance technology, applied in the field of new fire resistance modules and their manufacturing, can solve problems such as poor water resistance and non-compliance with fire protection requirements, and achieve the effects of convenient construction, high compressive strength and good oil resistance

Inactive Publication Date: 2011-03-16
浙江川科防保材料发展有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First, poor water resistance
After less than a day in the water test, it disperses into fine particles; secondly, when the combustion test is carried out, as the combustion proceeds, the expansion force generated by the expansion of the important materials will continuously disperse the module into fine particles, and finally bake It is called ash powder later, and the module disintegrates, which does not meet the fire protection requirements; third, because there is no flame retardant added to its polymer adhesive, it has a certain degree of fire resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A new type of fire retardant module in this embodiment includes the following components in parts by weight: expanded vermiculite 450; porcelain powder 308; water-based composite polymer flame retardant emulsion adhesive base material 639.8. The water-based composite polymer flame-retardant emulsion adhesive base material includes the following components in parts by weight: VAE280; IPP35; antimony white powder 4.8; water 320.

[0034] The manufacturing method of the novel fire retardant module of the present embodiment comprises the following steps:

[0035] a. Preparation of adhesive base material: put VAE, IPP, antimony white powder, and water into the disperser according to the above ratio and stir at high speed to disperse to form a water-based composite polymer flame-retardant emulsion adhesive base material;

[0036] b. Preparation of the main ingredients: Put the thermal insulation material expanded vermiculite and the adhesive material porcelain powder into the...

Embodiment 2

[0040] A new type of fire retardant module in this embodiment includes the following components in parts by weight: expanded vermiculite 455; diatomite 300; water-based composite polymer flame retardant emulsion adhesive base material 665. The water-based composite polymer flame-retardant emulsion adhesive base material includes the following components in parts by weight: white glue 290; TDCPP 40; antimony white powder 5; water 330.

[0041] The manufacturing method of the novel fire retardant module of the present embodiment comprises the following steps:

[0042] a. Preparation of adhesive base material: put white glue, TDCPP, antimony white powder, and water into the disperser according to the above ratio and stir at high speed to form a water-based composite polymer flame-retardant emulsion adhesive base material;

[0043] b. Preparation of the main ingredients: put the thermal insulation material expanded vermiculite and the adhesive material diatomaceous earth into the ...

Embodiment 3

[0047] A new type of fire retardant module in this embodiment includes the following components in parts by weight: expanded vermiculite 460; diatomite 295; water-based composite polymer flame retardant emulsion adhesive base material 680.3. The water-based composite polymer flame-retardant emulsion adhesive base material includes the following components in parts by weight: polyvinyl acetate 295; TDCPP 45; antimony white powder 5.3; water 335.

[0048] The manufacturing method of the novel fire retardant module of the present embodiment comprises the following steps:

[0049] a. Preparation of adhesive base material: put polyvinyl acetate, TDCPP, antimony white powder, and water into the disperser according to the above ratio and stir at high speed to form a water-based composite polymer flame-retardant emulsion adhesive base material;

[0050] b. Preparation of the main ingredients: put the thermal insulation material expanded vermiculite and the adhesive material diatomaceo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
water resistanceaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel fireproof module, which comprises the following components in part by weight: 450 to 460 parts of expanded vermiculite, 295 to 308 parts of high-temperature adhesive and 639.8 to 680.3 parts of aqueous composite macromolecular flame-retardant emulsion adhesive base material. The invention also discloses a preparation method for the novel fireproof module. The novel fireproof module has the characteristics of environment friendliness, high waterproof property and fireproof property.

Description

technical field [0001] The invention relates to a novel fire-blocking module and a manufacturing method thereof, belonging to the technical field of anti-corrosion materials. Background technique [0002] With the rapid development of my country's national economy and the intensification of modernization, energy problems have become increasingly prominent, and the production and use of electric energy have also increased significantly. Therefore, the construction of electric power production enterprises has also increased. The need for plugging is also increasing. At the same time, in order to improve the fire resistance requirements of fire prevention and sealing, domestic units have developed a new generation of fire resistance module products with convenient construction for the market. In order to keep up with the pace of the market, the domestic fire-blocking module was tested and analyzed, and it was found that the fire-blocking module was not as perfect as advertised,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 袁雪祥董立明周璐
Owner 浙江川科防保材料发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com