Control method of steel cast ending

A control method and technology for casting steel, applied in the field of control, can solve the problems of Als loss, reduce the yield of finished products, increase the loss of steel materials, etc., and achieve the effects of controlling the pouring time, improving the quality of the finished product, and reducing the accident rate.

Active Publication Date: 2012-12-19
ANGANG STEEL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the phenomenon of remaining steel in the large tank, it will lead to an increase in the loss of steel materials and reduce the yield of finished products; for the slag in the large tank, the oxidative converter slag will cause secondary oxidation in the tundish, which will promote the loss of Als in molten steel and increase the yield of steel. Al in water 2 o 3 The content of inclusions not only blocks the submerged nozzle, but also directly reduces the cleanliness of molten steel, increasing the probability of defects such as product inclusions and cracks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A method for controlling the finish of pouring steel, adopting the following steps:

[0013] 1. Accurately control the quality of the empty steel ladle, the slag amount of the converter, the loading amount of the converter, the tapping amount and the control accuracy of the slab length measurement system to ensure the accuracy of the theoretical tapping amount and the slab length data.

[0014] 2. According to the formula: strand length = (theoretical pouring molten steel amount × 1.018) / (T × W × 7.85) to calculate the length of the slab, when using this calculation formula, ensure that the quality of the tundish is maintained at the end of each large tank pouring constant.

[0015] 3. Calculate the quality of the produced slab according to the length of the slab.

[0016] 4. Subtract the produced slab quality from the total mass of poured molten steel to obtain the remaining molten steel quality of the large tank, and control the pouring time according to the remain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shrinkage factoraaaaaaaaaa
Login to view more

Abstract

The invention relates to a control method of steel cast ending, which comprises the steps of: calculating a cast blank length according to a formula that the cast flow length=(theoretical molten steel casting quantity*cast blank contraction coefficient) / (T*W*7.85); then figuring out the mass of a produced cast blank according to the cast blank length; and finally, subtracting the mass of the produced cast blank by the total mass of the cast molten steel to obtain the mass of surplus molten steel in a large tank, i.e. controlling the casting time according to the mass of the surplus molten steel. The method is simple in operation; according to the method, the mass of the surplus molten steel can be rapidly known, slag is prevented from roughing at the last casting stage of the large tank, the requirement on continuous casting production is greatly met, the quality of finished products is high, and the enterprise benefit is improved.

Description

technical field [0001] The invention relates to a control method, in particular to a control method for steel casting. Background technique [0002] At present, due to the failure of the weighing equipment on the rotary table of the molten steel tank during the continuous casting pouring process, during the pouring process of the large tank, the on-site operator’s judgment on the end of the pouring of the large tank mainly depends on the pouring time, but due to the There are certain differences in the molten steel quality of different molten steel tanks among different heats. At the same time, during the continuous casting process, abnormal conditions such as temporary speed change operation, water port change, and leakage prediction often occur. Changes directly lead to inaccurate judgment of the end point of pouring steel in large tanks based on time. In the actual production process, the phenomenon of leftover steel in large tanks or slag in large tanks often occurs. F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D37/00B22D11/18
Inventor 简龙温铁光魏元王鹏吴世龙张志文安连旗
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products