Method for producing color-spun and hollow yarns

A production method, hollow technology, applied in the direction of yarn, textiles and papermaking, can solve the problems that yarn affects warping and weaving, restricts development, and yarn strength affects weaving, etc.

Inactive Publication Date: 2011-05-04
SHANDONG DAIYIN TEXTILE GROUP SHARE CO LTD
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The characteristics of its yarn formation are light, bulky and soft. However, during the sizing process, the water-soluble vinylon will shrink when heated, and the strength of the yarn will be greatly reduced, which will affect weaving.
Especially in the yarn-dyed industry, the yarn must be dyed before weaving. During the dyeing process, vinylon will dissolve, and the strength of the yarn will also decrease, which will affect warping and weaving. Therefore, the hollow yarn has not been used in weaving and weaving. The dyed weaving industry has been well developed and utilized, which limits the further development of the market for such products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing color-spun and hollow yarns

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The present invention will be further described below in conjunction with embodiment:

[0014] The technological process of described embodiment is:

[0015] Colored cotton slivers are dyed, dehydrated, dried, packed, plucked, mixed, opened, rolled, and carded to form colored cotton slivers; vinylon fibers are plucked, mixed, sent, rolled, and carded Form vinylon sliver; draw colored cotton raw sliver and vinylon sliver at a quantity ratio of 80:20 to form a mature sliver, mix and draw the sliver, and then produce excellent spinning hollow yarn through roving and spun yarn.

[0016] Treatment of colored sliver: after raw cotton is dyed into black, yellow, blue, green, etc., it is mixed with white cotton according to a certain mixing ratio according to product requirements, and the proportion of colored cotton is 5%-50% to form colored sliver after loose fiber dyeing , dehydration, drying, packing, plucking, mixing, opening, rolling, and carding to form colored cotton s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing color-spun and hollow yarns, which is novel hollow yarn and color-spun yarn integrated spinning technology. The colored-cotton fibers are subjected to loose stock dyeing, and are coiled by a clear cotton machine, and slivered by a slivering machine; the silvered colored-cotton fibers and the vinylon fibers silvered by carding are folded on a drawing frame, rough yarns are spun by a coarse spinner, and the color-spun and hollow yarns are spun by a spinning frame. In the method, the problem that water-soluble vinylon is heated and shrunk and the strong force of yarns is greatly reduced so as to influence weaving in the process of weaving and starching the hollow yarns is effectively solved.

Description

technical field [0001] The invention relates to a yarn production method, in particular to a production method of colored spinning hollow yarn. Background technique [0002] Hollow yarn is composited with water-soluble fiber (generally vinylon fiber) made by composite spinning technology and solvent wet gel spinning method. Its structure is cotton in the outer layer and water-soluble fiber in the inner layer to form a double layer. structure. After adjusting the spinning process, the water-soluble fiber is effectively and evenly coated on the inner side of the cotton fiber, and then after post-processing (removal), the inner fiber is dissolved to form a ring-shaped hollow yarn. The characteristics of its yarn formation are light, bulky and soft. However, during the sizing process, the water-soluble vinylon will shrink when heated, and the strength of the yarn will be greatly reduced, which will affect weaving. Especially in the yarn-dyed industry, the yarn must be dyed bef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D02G3/36
Inventor 赵焕臣李广军谢松才王长青亓焕军李宗林杨延瑞
Owner SHANDONG DAIYIN TEXTILE GROUP SHARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More