Exterior wall paint
A technology for exterior wall paint and preservative, applied in the field of coatings and paints, and exterior wall paint, can solve the problems of reducing the performance of exterior wall paint, easy to corrode, and high production cost, preventing corruption and demulsification, improving storage period, and high efficiency. The effect of bactericidal properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] 1. Slowly add 2 parts of cellulose under low-speed stirring, stir for 10 minutes, add 1 part of ammonia water, continue stirring for 30 minutes, until the cellulose is completely dissolved, add 3 parts of Pengrun soil and continue stirring for 15 minutes until it is completely dissolved.
[0012] 2. Add wetting agent (T283), 1 part; ethylene glycol, 9 parts; high-viscosity agent, 2 parts, and stir for 5 minutes until uniform.
[0013] 3. Add 100 parts of titanium dioxide, 400 parts of calcium, and 60 parts of talcum powder in turn under stirring. When each powder is added, it should be completely wet before adding the next bag.
[0014] 4. After adding the powder, stir at high speed for 30 minutes.
[0015] 5. The paint pulp is passed through 60 meshes and put into the transfer tank.
[0016] 6. Grind until the fineness is below 70um, and pour into the diluting tank.
[0017] 7. Use a diaphragm pump to pour the emulsion into the paint slurry, and add preservative (Can...
Embodiment 2
[0019] 1. Slowly add 2.3 parts of cellulose under low-speed stirring, stir for 10 minutes, add 1.5 parts of ammonia water, continue stirring for 30 minutes, until the cellulose is completely dissolved, add 4 parts of Pengrun soil and continue stirring for 15 minutes until it is completely dissolved.
[0020] 2. Add wetting agent (T283), 1.5 parts; ethylene glycol, 10 parts; high-viscosity agent, 3 parts, and stir for 5 minutes until uniform.
[0021] 3. Add 110 parts of titanium dioxide, 450 parts of calcium, and 70 parts of talcum powder in turn under stirring. When each powder is added, it should be completely wet before adding to the next bag.
[0022] 4. After adding the powder, stir at high speed for 30 minutes.
[0023] 5. The paint pulp is passed through 60 meshes and put into the transfer tank.
[0024] 6. Grind until the fineness is below 70um, and pour into the diluting tank.
[0025] 7. Use a diaphragm pump to pour the emulsion into the paint slurry, and add prese...
Embodiment 3
[0027] 1. Slowly add 2.5 parts of cellulose under low-speed stirring, stir for 10 minutes, add 2 parts of ammonia water, continue stirring for 30 minutes, until the cellulose is completely dissolved, add 6 parts of Pengrun soil and continue stirring for 15 minutes until it is completely dissolved.
[0028] 2. Add wetting agent (T283), 2 parts; ethylene glycol, 11 parts; high-viscosity agent, 4 parts, and stir for 5 minutes until uniform.
[0029] 3. Add 120 parts of titanium dioxide, 500 parts of calcium, and 80 parts of talcum powder in turn under stirring. When each powder is added, it should be completely wet before adding the next bag.
[0030] 4. After adding the powder, stir at high speed for 30 minutes.
[0031] 5. The paint pulp is passed through 60 meshes and put into the transfer tank.
[0032] 6. Grind until the fineness is below 70um, and pour into the diluting tank.
[0033] 7. Use a diaphragm pump to pour the emulsion into the paint slurry, and add preservative...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap