A technology of dope dyeing and polyester, which is applied in knitting, weft knitting, fabric surface trimming, etc. It can solve the problems of difficult moisture emission, low color fastness, polyester air permeability and poor hygroscopicity, and achieve high temperature washing color fastness Large size, simple processing technology, and high color fastness to sunlight

Inactive Publication Date: 2011-08-17
BOYANG COMPOSITE FABRIC TECH KUSN
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, post-dyed polyester needle terry fabrics generally have a color fastness to sunlight lower than grade 5, and a color fastness to washing at 60°C is lower than grade 3.
In addition, polyester has poor air permeability and hygroscopicity. After wearing for a long time, the clothes made of polyester will not easily emit moisture and easily produce odor.
Warm polyester loop brushed fabric, when worn, due to the friction of the body, the fabric will generate static electricity and pilling on the surface of the fabric, which will affect the appearance and service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Raw liquor coloring terylene terry knitted fabrics
  • Raw liquor coloring terylene terry knitted fabrics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Specific embodiments of the present invention will be further described in detail below.

[0016] Such as figure 1 As shown, the dope dyed polyester needle terry fabric of the present invention is woven from three yarns by a double-sided circular terry knitting machine: the yarn 1 composed of polyester coconut carbon yarn is woven into a uniform grid-shaped basic structure ; The yarn 2 composed of dope dyed polyester fiber and polyester carbon fiber is interwoven with the basic weave to form a front pile protruding on one side of the basic weave; the yarn 3 composed of polyester carbon fiber and polyester coconut carbon yarn is also jointly formed with the basic weave The weaves interweave to form reverse loops that protrude from the other side of the basic weave.

[0017] Among them, the color fastness to sunlight of the dope-dyed polyester fiber is higher than grade 6, and the color fastness to washing at 60°C is higher than grade 4. This makes the processed fabric ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses raw liquor coloring terylene terry knitted fabrics. The raw liquor coloring terylene terry knitted fabrics contain raw liquor coloring terylene fibers and have the characteristics that: the raw liquor coloring terylene terry knitted fabrics also contain terylene cocona yarns and permanently conductive terylene carbon fibers, and the raw liquor coloring terylene fibers, terylene cocona yarns and terylene carbon fibers jointly form a double-face terry structure. In the invention, the raw liquor coloring terylene fibers, terylene cocona yarns and terylene carbon fibers undergo blended weaving to produce the double-face terry fabrics, which not only keep original advantages of the terylene materials, namely the color fastness to daylight exposure and the color fastness to high-temperature water washing are both high, but also have the advantages of static resistance, no balling-up, moisture absorption and the like. In addition, the raw liquor coloring terylene terry knitted fabrics also have the advantages of simple processing technology, high durability and the like.

Description

[0001] technical field [0002] The invention belongs to the field of textiles, and in particular relates to a deodorizing and anti-pilling polyester terry brushed fabric. Background technique [0003] Polyester is a very common synthetic fiber. Because of its excellent setting performance, it is widely used in the manufacture of clothing fabrics. After the polyester fabric is set, it can still maintain its original shape after being washed many times in use. In addition, it also has the advantages of high strength, good elasticity, heat resistance, corrosion resistance and so on. However, at present, post-dyed polyester needle terry fabrics generally have a color fastness to sunlight lower than grade 5, and a color fastness to washing at 60°C is lower than grade 3. In addition, polyester has poor air permeability and hygroscopicity. After wearing for a long time, the clothes made of polyester will not easily emit moisture and easily produce odor. Warm polyester loop bru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/04D04B1/14D06C11/00D06C13/00
Inventor 杨昭福
Owner BOYANG COMPOSITE FABRIC TECH KUSN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap