Method for recycling thermoplastic polypropylene plastic parts of scraped automobile

A technology for polypropylene plastics and scrapped cars, which is applied in plastic recycling and recycling technology, and can solve the problems of low added value of remanufacturing, low feasibility of mixed recycling and remanufacturing methods, narrow industrial application range, etc., and achieve good comprehensive performance Effect

Inactive Publication Date: 2011-09-07
路洪洲 +3
View PDF9 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] In addition, after mixing and crushing various plastic parts of scrapped cars, various materials are mixed together, such as materials mixed with PP, ABS, PVC, and PC. The performance of various plastics is quite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recycling thermoplastic polypropylene plastic parts of scraped automobile
  • Method for recycling thermoplastic polypropylene plastic parts of scraped automobile
  • Method for recycling thermoplastic polypropylene plastic parts of scraped automobile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Manually disassemble scrapped cars, remove bumpers, instrument panels, door trim panels, lights and other interior and exterior plastic and structural parts, and classify thermoplastic components into ABS, PP, PC, PVC materials, etc. Remove the metal links (such as screws, etc.) as far as possible, and control the impurity purity of the sorted PP material parts below 1%; use two-stage crushing, use a large crusher for coarse crushing, use a 6mm screen, and crush the particle size to 6mm or less, in order to improve the crushing efficiency, use a shearing crusher for fine crushing, use a 1mm screen, and finally crush to less than 1mm to obtain a thermoplastic polypropylene plastic powder mixture less than 1mm, and then separate the metal debris by ferromagnetic separation , and then carry out high-voltage electrostatic sorting, high-voltage electrostatic sorting adopts double-roller corona discharge high-voltage electrostatic sorting machine, corona electrode adopts wire ...

Embodiment 2

[0050] Manually disassemble scrapped cars, remove bumpers, instrument panels, door trim panels, lights and other interior and exterior plastic and structural parts, and classify thermoplastic components into ABS, PP, PC, PVC materials, etc. Remove the metal links (such as screws, etc.) as far as possible, and control the impurity purity of the sorted PP material parts below 1%; adopt two-stage crushing, use a large crusher for coarse crushing, use a 12mm screen, and crush the particle size to 12mm, in order to improve the crushing efficiency, use a shearing crusher for fine crushing, use a 1mm screen, and finally crush to less than 1mm to obtain a thermoplastic polypropylene plastic powder mixture less than 1mm, and then perform ferromagnetic separation to separate metal debris, Then carry out high-voltage electrostatic sorting, high-voltage electrostatic sorting adopts double-roller corona discharge high-voltage electrostatic sorting machine, corona electrode adopts wire elect...

Embodiment 3

[0052] Disassemble scrapped cars, remove bumpers, instrument panels, door trim panels, lights and other interior and exterior plastic and structural parts, and classify thermoplastic components according to ABS, PP, PC, PVC materials, etc. Remove metal links as much as possible (such as screws, etc.), and control the impurity purity of the sorted PP material parts below 1%; adopt two-stage crushing, use a large crusher for coarse crushing, and use an 8mm screen to crush the particle size to 6~ 8mm or less, in order to improve the crushing efficiency, use a shearing crusher for fine crushing, use a 2mm screen, and finally crush to less than 2mm, screen out the thermoplastic polypropylene plastic powder mixture less than 1mm, and then separate the metal fragments by ferromagnetic separation Chips, and then carry out high-voltage electrostatic sorting, high-voltage electrostatic sorting adopts a double-roller corona discharge high-voltage electrostatic sorting machine, the corona ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of recycling of waste plastics of scraped automobiles, and relates to a method for recycling thermoplastic polypropylene plastic parts of a scraped automobile. The method comprises the following steps of: manually disassembling nonmetallic inner and outer ornaments and structural parts of the scraped automobile, manually sorting thermosetting plastic parts and thermoplastic plastic parts, further manually sorting the thermoplastic polypropylene plastic parts, manually disassembling and separating metallic linkage parts, circuits and the like of the sorted thermoplastic polypropylene plastic parts, performing two-stage crushing on the polypropylene plastic parts, performing ferromagnetic sorting on two crushed materials respectively to separate out metallic scraps, separating out fine metallic scraps and metallic paint by using a roller direct-current high-voltage corona and electrostatic composite electric field sorter, performing sampling performance detection on the cleaned and dried materials, adding a modifier according to the detection results and the using requirements, granulating, and manufacturing automobile plastic members by using the materials. By using the method, the plastic recycling problem of the scraped automobile is solved, broken plastic resources of the scraped automobile are recycled, environmental pollution is avoided, the energy consumption is low, and the additional value is high.

Description

technical field [0001] The invention belongs to the field of recycling and remanufacturing of waste plastics from scrapped automobiles, and relates to a method for remanufacturing plastics required by automobile components through a series of processes by utilizing waste plastic parts of scrapped automobiles. Background technique [0002] With the improvement of people's awareness of environmental protection, it is required to recycle scrapped automobile materials, especially scrapped automobile waste plastics that pollute the environment. The "Automotive Product Recycling Technology Policy" issued in 2006 requires the establishment of a classified collection and sorting system for scrapped automotive materials and substances, and a complete recycling, processing, and utilization system for automotive renewable resources. The goal of the first stage: from 2010, the recycling rate of all domestic and imported M2 and M3, N2 and N3 vehicles should reach about 85%, and the recyc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29B17/00
CPCY02W30/62
Inventor 路洪洲洪贤军路贵民许振明
Owner 路洪洲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap