Hydrogel for use in downhole seal applications

a technology of hydrogel and seal, which is applied in the direction of sealing/packing, other chemical processes, borehole/well accessories, etc., can solve the problems of water starting to absorb and swell, and achieve the effect of preventing seal failure and high swelling for

Inactive Publication Date: 2005-08-04
SCHLUMBERGER TECH CORP
View PDF10 Cites 126 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0011] Once incorporated into the seal body, the hydrogel provides several advantages over typical seal body components. First, the hydrogel allows the seal be to energized via swelling. Since hydrogel can swell as much as 1,000 times in volume, high swelling force can be utilized to energize the main seal body as well as anti-extrusion device.
[0012] The hydrogel may als

Problems solved by technology

That is, whenever it contacts an aqueous m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogel for use in downhole seal applications
  • Hydrogel for use in downhole seal applications
  • Hydrogel for use in downhole seal applications

Examples

Experimental program
Comparison scheme
Effect test

example 1

Packer Elements

[0029]FIG. 1 shows three-piece rubber element array or packer element 10, such as that commonly used in downhole packers. The packer elements are external packer seals that seal the annulus space between tubing and casing (not shown). Elements are energized by axial deflection of the seals after the packer is run into the hole. Commonly used packer elements typically consist of backup end rings 16 and a center seal or element 18. The center seal 18 typically includes a ring 20 which establishes the inner diameter of the seal. Hydrogel may be included or incorporated into any or all of the seal elements. The hydrogel allows the seals to be energized in response to external stimuli, as previously described.

[0030]FIG. 2 shows a garter spring element array 50. The array 50 includes a main element or seal 52, a garter spring 54 and backup end rings 56. The array also includes an ID ring 58. Hydrogel may be included in any or all of the seals of the array. As with the ass...

example 2

O-Ring

[0032] O-rings are simple bi-directional static seals. For high temperature and / or high pressure sealing applications, backup rings are used to prevent O-ring extrusion. As shown in FIG. 4, the o-ring 150 includes two backup rings 152 which are formed of thermoplastic materials blended with hydrogel polymer. The O-ring may also be formed of elastomers blended with hydrogel polymer. In this application, the hydrogel is able to seal off potential leak paths as well as keep the o-ring energized via swelling. These characteristics are not achievable with existing conventional rubber materials used for o-ring applications.

example 3

T-Seal

[0033] T-seals are typically used as reciprocating bi-directional dynamic seals. As shown in FIG. 5, T-seal 200 including seal body 202 and retaining ring 204. The seal body is formed of a hydrogel modified thermoplastic or elastomer. Hydrogel can seal off potential leak paths as well as keep the T-seal energized via swelling. These benefits are not achievable with existing conventional rubber materials used for T-seal application.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermoplasticityaaaaaaaaaa
Login to view more

Abstract

The present invention is a composition for forming seals. The composition includes a base material and a hydrogel. The base materials is preferably an elastomer or a thermoplastic. Seals formed with the composition are particularly suited for use in a wellbore environment. The inclusion of hydrogel in the seals allows the seals to be manipulated or altered through certain environmental factors. For instance, temperature, oil/water ratio, pH and the electronic field may all be used to alter the characteristics of the hydrogel. In this way, the seal may be caused to swell in response to a specific stimulus, thereby preventing or sealing a leak without requiring additional work or input from the operator.

Description

REFERENCE TO RELATED PROVISIONAL APPLICATION [0001] This application claims the benefit of U.S. Provisional Application Ser. No. 60 / 541,035.BACKGROUND OF THE INVENTION [0002] 1. Field of the Invention [0003] The present invention relates generally to seals for oilfield applications. More specifically the present invention describes the use of hydrogel in seals for downhole use. [0004] 2. Description of the Prior Art [0005] Seals, including o-rings, packer elements, Chevron seals, gaskets, etc., are widely used for numerous downhole oilfield applications. One ongoing issue in this area is how to energize seals and maintain sealing forces throughout seal service life. Capital loss or remediation associated with seal failure can be tremendous in certain operation areas. [0006] One conventional method to energize seal is to utilize mechanical force to deform seal between sealing surfaces. For seals with large cross-section and / or large sealing gaps, satisfactory sealing performance is h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L1/28C08L5/14C09K3/10E21B33/12
CPCC08L1/28C08L5/14C08L101/00C08L101/14C09K3/10C09K2200/06C09K2200/0617E21B33/12C09K2200/0627C09K2200/0632C09K2200/0657C09K2200/0685C08L2666/06C08L2666/02C08L2666/08C08L2666/26
Inventor LI, YANMEIZHOU, JIAN
Owner SCHLUMBERGER TECH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap