Method for synchronously roughening both surfaces of electrolytic copper foil and equipment thereof

Abstract

The invention relates to a method for synchronously roughening and solidifying both surfaces of an electrolytic copper foil and equipment thereof, which belong to the technical field of electrolytic copper foils. The technical key point is that: corresponding anode plates are arranged on a smooth surface and a rough surface and electrolyte flows through the space between the electrolytic copper foil and the anode plates when the electrolytic copper foil passes through a roughening groove and a solidifying groove so as to perform electroplating copper precipitation treatment on the smooth surface and the rough surface of the electrolytic copper foil synchronously at a time, wherein the electroplating anode plates in the roughening groove and the solidifying groove of the used equipment are distributed in the middle and on the front side of a groove body. Compared with the prior art, the method for synchronously roughening and solidifying both surfaces of the electrolytic copper foil and the used equipment thereof have the advantages that: the smooth surface and the rough surface of the copper foil can be synchronously electroplated at a time, so that production efficiency is improved, and energy consumption is reduced.

Description

technical field [0001] The invention relates to a method for roughening and curing electrolytic copper foil, in particular to a method for simultaneous roughening and curing of both sides of electrolytic copper foil. The invention also relates to equipment for synchronous roughening and curing of both sides of electrolytic copper foil, which belongs to electrolytic copper foil technology field. Background technique [0002] Compared with the electrolytic copper foil for copper-clad laminates, the double-sided roughened electrolytic copper foil for lithium-ion power batteries has a large difference in performance indicators. The mechanical measurement thickness of double-sided roughened electrolytic copper foil for lithium-ion power batteries is ≤12 microns, Smooth and matte crystal structures are dense and uniform, roughness of the matte surface is ≤2.5 microns, metal density is close to the theoretical density of copper, elongation is ≥5%, and tensile strength is ≥400N / mm ...

AI Technical Summary

Problems solved by technology

[0003] At present, the anode of the equipment used in the production of double-sided roughened electrolytic copper foil surface is as follows: figure 1 As shown, the anodes are distributed on both sides of the tank, and the solution flow distribution of the liquid in the tank is as follows figure 2 As shown, the smooth surface of the copper foil is treated first, and then the rough surface of the copper foil is treated in reverse. However, the production cost is high and the energy consumption is high, which brings many problems to the manufacturer.

Images