Pipeline steel with a thickness of ≥25mm for deep sea and its production method

A pipeline steel and deep-sea technology, which is applied in the field of deep-sea pipeline steel and its production, can solve the problems of complex production process, high production cost, and difficult performance, and achieve the effects of economical component design, production cost reduction, and simple production process.

Active Publication Date: 2011-12-14
武汉钢铁有限公司
View PDF6 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The object of the present invention is to provide a yield strength R t0.5 ≥450MPa, -40℃KV 2 ≥200J, -20℃ DWTT SA≥85%, and yield strength ratio R t0.5 / R m ≤0.85, elongation A 50mm ≥40%, uniform elongation A gt ≥10% deep-sea use ≥25mm thick pipeline steel and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pipeline steel with a thickness of ≥25mm for deep sea and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] 28mm thick pipeline steel for deep sea, its composition and weight percentage are: C: 0.025%, Si: 0.50%, Mn: 1.60%, P: 0.014%, S: 0.0020%, Ni: 0.01%, Mo: 0.30% , Cr: 0.05%, Cu: 0.03%, Nb: 0.031%, V: 0.004%, Ti: 0.01%, Al: 0.011%, N: 0.009%, Ca: 0.0034%, the weight percentage of residual element control is: As : 0.008%, Sb: 0.001%, Sn: 0.002%, Pb: 0.001%, Bi: 0.003%, B: 0.0001%, the balance is Fe and other unavoidable impurities;

[0045] Welding cold crack sensitivity coefficient Pcm=C+Si / 30+(Mn+Cu+Cr) / 20+Mo / 15+Ni / 60+V / 10+5B=0.147%;

[0046] Nb: 0.031% + V: 0.004% + Ti: 0.010% = 0.045%.

[0047] The method for producing 28mm thick pipeline steel for deep sea, the steps:

[0048] 1) Smelting and continuous casting into billets according to the clean steel process;

[0049] 2) Heating the continuous casting slab, and controlling the heating temperature to be 1120-1125°C;

[0050] 3) Carry out rough rolling, control the rolling start temperature at 1075-1180°C, end tem...

Embodiment 2

[0058] 25.4mm thick pipeline steel for deep sea, its composition and weight percentage are: C: 0.040%, Si: 0.32%, Mn: 1.52%, P: 0.012%, S: 0.0025%, Ni: 0.07%, Mo: 0.05 %, Cr: 0.22%, Cu: 0.02%, Nb: 0.040%, V: 0.01%, Ti: 0.007%, Al: 0.021%, N: 0.0070%, Ca: 0.0048%, the weight percentage of residual element control is: As: 0.009%, Sb: 0.001%, Sn: 0.001%, Pb: 0.0007%, Bi: 0.004%, B: 0.0001%, the balance is Fe and other inevitable impurities;

[0059] Welding cold crack sensitivity coefficient Pcm=C+Si / 30+(Mn+Cu+Cr) / 20+Mo / 15+Ni / 60+V / 10+5B=0.145%.

[0060] Nb: 0.040% + V: 0.01% + Ti: 0.007% = 0.057%.

[0061] The method for producing pipeline steel with a thickness of 25.4mm for deep sea, the steps:

[0062] 1) Smelting and continuous casting into billets according to the clean steel process;

[0063] 2) Heating the continuous casting slab, and controlling the heating temperature to be 1145-1150°C;

[0064] 3) Carry out rough rolling, control the rolling start temperature at 111...

Embodiment 3

[0072] 27mm thick pipeline steel for deep sea, its composition and weight percentage are: C: 0.048%, Si: 0.25%, Mn: 1.37%, P: 0.010%, S: 0.0011%, Ni: 0%, Mo: 0.07% , Cr: 0.28%, Cu: 0.05%, Nb: 0.058%, V: 0.003%, Ti: 0.015%, Al: 0.032%, N: 0.006%, Ca: 0.0025%, the weight percentage of residual element control is: As : 0.008%, Sb: 0.0008%, Sn: 0.0006%, Pb: 0.0009%, Bi: 0.003%, B: 0.0001%, the balance is Fe and other unavoidable impurities;

[0073] Welding cold crack sensitivity coefficient Pcm=C+Si / 30+(Mn+Cu+Cr) / 20+Mo / 15+Ni / 60+V / 10+5B=0.147%;

[0074] Nb: 0.058% + V: 0.003% + Ti: 0.015% = 0.076%.

[0075] The method for producing 27mm thick pipeline steel for deep sea, the steps:

[0076] 1) Smelting and continuous casting into billets according to the clean steel process;

[0077] 2) Heating the continuous casting slab, and controlling the heating temperature to be 1225-1230°C;

[0078] 3) Carry out rough rolling, control the rolling start temperature to 1165-1170°C, end te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a pipeline steel for deep sea and a production method thereof. The pipeline steel for deep sea comprises the following components in percentage by weight: 0.025-0.080% of C, 0.05-0.50% of Si, 1.20-1.60% of Mn, less than or equal to 0.015% of P, less than or equal to 0.003% of S, 0.05-0.30% of Mo, 0.03-0.06% of Nb, 0.005-0.025% of Ti, 0.01-0.04% of Al, less than or equal to 0.010% of N and 0.0010-0.0050% of Ca used as main components, and less than or equal to 0.03% of As, less than or equal to 0.01% of Sb, less than or equal to 0.02% of Sn, less than or equal to 0.01%of Pb, less than or equal to 0.01% of Bi and less than or equal to 0.0005% of B used as residual elements. The production method comprises the following production steps: smelting according to clean steel, and carrying out continuous casting to obtain a blank; heating the cast blank; carrying out rough rolling; carrying out fine rolling; relaxing; cooling; relaxing again; straightening; and carrying out air cooling to room temperature. The pipeline steel has simple ingredient and technology, the thickness of the pipeline steel is more than or equal to 25mm, and the pipeline steel is used for deep sea pipelines. The Rt05 of the pipeline steel is more than or equal to 450MPa, Rm is more than or equal to 550MPa, Rt05 / Rm is less than or equal to 0.85, A50mm is more than or equal to 40%, Agt is more than or equal to 10%, -40DEG C KV2 is more than or equal to 200J, and -20DEG C DWTT (Drop-Weight Tear Test) SA is more than or equal to 85%.

Description

technical field [0001] The invention relates to steel for pipelines and a production method thereof, in particular to pipeline steel for deep sea use and a production method thereof. Background technique [0002] With the gradual depletion of land oil and gas resources, new resource exploitation extends to areas with harsh geological conditions such as oceans and polar regions. At present, it has been proven that the world's offshore oil resources account for 34% of the world's total oil resources, and the annual production of offshore natural gas has reached 32% of the world's total annual natural gas production. More than 100 countries around the world are conducting offshore oil exploration, of which More than half of the oil exploration has been carried out in the deep sea. Therefore, the importance of the development and application of steel for submarine pipelines, especially steel for deep-sea pipelines, has become increasingly prominent. At present, domestic steel f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14C21D8/02
Inventor 徐进桥郭斌郑琳董中波彭涛陈洪伟邹德辉张开广
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com