Polylactic acid/ polyamide 11 alloy material
An alloy material, polylactic acid technology, which is applied in the direction of conjugated synthetic polymer rayon, chemical characteristics of fibers, textiles and papermaking, etc. It can improve the mechanical properties of impact toughness, high modulus and tensile strength, and low dependence on petrochemical resources.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] Example 1-12
[0038] Polylactic acid (PLA), nylon 11 (PA11) and elastomer (EGMA-g-SAN) were dried in a vacuum oven at 80°C for 24 hours. PLA / Nylon 11 and elastomer were weighed according to the mass ratio in Table 1. After mixing and stirring at room temperature, it is added to the internal mixer, the internal mixer temperature is 200°C, the screw speed is set to 100 rpm, and the material is discharged after 5 minutes of mixing.
[0039] The above-mentioned mixed samples were hot pressed into a sheet with a thickness of 1 mm in a hot press at 210° C., and standard test specimens were prepared with a standard dumbbell-shaped punching knife for performance testing. The results are shown in Table 1.
Example Embodiment
[0044] Example 13
[0045] After polylactic acid (PLA), nylon 11 (PA11) and elastomer (EGMA-g-SAN) are dried in a vacuum oven at 80°C for 24 hours, a quantitative amount of PLA and EGMA-g-SAN are first mixed and then added to the internal mixer , The internal mixer temperature is 200℃, the screw speed is set to 100rpm, and the material is discharged after 5 minutes of mixing. The sample was pulverized and mixed with a quantitative nylon 11, added to an internal mixer, the temperature of the internal mixer was 200°C, the screw speed was set to 100 rpm, and the material was discharged after banburying for 5 minutes. The mass ratio of the three raw materials used is PLA / nylon 11=55g / 45g, and EGMA-g-SAN is 6% of the total mass of PLA and nylon 11.
[0046] The above-mentioned mixed samples were hot pressed into a sheet with a thickness of 1 mm in a hot press at 210° C., and standard test specimens were prepared with a standard dumbbell-shaped punching knife for performance testing. Th...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap