Degradable pressure-sensitive adhesive and preparation method thereof

A pressure-sensitive adhesive, complete dissolution technology, applied in adhesive types, non-polymer adhesive additives, unsaturated alcohol copolymer adhesives, etc., can solve environmental pollution, non-degradable and other problems, and achieve stickiness , low cost and simple preparation process

Inactive Publication Date: 2013-01-16
庄晓曦
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above types of pressure-sensitive adhesives have certain advantages and applications, they are not degradable and easily pollute the environment. Therefore, there is an urgent need for degradable pressure-sensitive adhesives to appear.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Add 100 parts of polyvinyl alcohol resin, 40 parts of 2-ethylbenzofuran, and 5 parts of stearic acid to 200 parts of acetone to dissolve completely, then add 18 parts of glycerin, 12 parts of magnesium oxide and 20 parts of filler, and mix well Prepared into a viscous adhesive. The 90-day degradation rate was 79% based on the amount of carbon dioxide released.

Embodiment 2

[0018] 140 parts of polyvinyl alcohol resin, 60 parts of 2-ethylbenzofuran, and 8 parts of stearic acid were added to 400 parts of acetone to dissolve completely, then 16 parts of glycerin, 18 parts of magnesium oxide and 30 parts of filler were added, and mixed well Prepared into a viscous adhesive. The 90-day degradation rate was 80% based on the amount of carbon dioxide released.

Embodiment 3

[0020] Add 120 parts of polyvinyl alcohol resin, 30 parts of 2-ethylbenzofuran, and 6 parts of stearic acid into 300 parts of acetone to dissolve completely, then add 20 parts of glycerin, 16 parts of magnesium oxide and 25 parts of filler, and mix well Prepared into a viscous adhesive. The 90-day degradation rate was 80% based on the amount of carbon dioxide released.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a degradable pressure-sensitive adhesive and a preparation method thereof. The degradable pressure-sensitive adhesive is prepared from the following components in part by weight: 90 to 140 parts of polyvinyl alcohol resin, 30 to 60 parts of 2-ethyl benzofuran, 12 to 18 parts of magnesium oxide, 16 to 20 parts of glycerol, 5 to 8 parts of stearic acid, 20 to 30 parts of filler and 160 to 500 parts of acetone. The preparation method comprises the following steps of: adding the polyvinyl alcohol resin, the 2-ethyl benzofuran and the stearic acid into the acetone at the temperature of between 50 and 90 DEG C and dissolving completely; adding the glycerol, the magnesium oxide and the filler; and mixing uniformly to obtain the degradable pressure-sensitive adhesive. The main component of the pressure-sensitive adhesive is the polyvinyl alcohol resin which can be biodegraded completely; the 2-ethyl benzofuran can enhance the viscosity of the polyvinyl alcohol resin; and in the presence of the magnesium oxide, the viscosity of the polyvinyl alcohol resin can be enhanced and biodegradation of the viscosity of the polyvinyl alcohol resin can be promoted. The pressure-sensitive adhesive maintains the viscosity, overcomes the defects in the aspect of environmental protection and is a degradable pressure-sensitive adhesive. In addition, the preparation process is simple and the cost is low.

Description

technical field [0001] The invention relates to a pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] After 20 years of rapid development in the pressure-sensitive tape industry, both production, product range, and product competitiveness in the market are on the rise. The main products include: packaging tape, electrical insulation tape, surface protection tape, double-sided tape, masking tape, medical tape, anti-corrosion tape, label paper. [0003] The main varieties of pressure-sensitive adhesives produced in China are: acrylic pressure-sensitive adhesives, rubber-type pressure-sensitive adhesives and hot-melt pressure-sensitive adhesives. [0004] Pressure-sensitive adhesives are used in various fields of daily life. Different fields have different requirements for the performance of pressure-sensitive adhesives. Therefore, various modifications of pressure-sensitive adhesives are often required to make them suitable for this fie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J129/04C09J11/06C09J11/04
Inventor 庄晓曦
Owner 庄晓曦