Multifunctional water-soluble adhesive cement for replacing gasoline adhesive cement

A glue, water-based technology, used in adhesives, natural rubber adhesives, adhesive types, etc., can solve the problems of low bonding strength, harm to human health, pollute the environment, etc., and achieve high strength and good bonding effect. , the effect of saving a long time

Inactive Publication Date: 2014-05-28
江西省新视野实业发展有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] my country's rubber products industry has been using gasoline and toluene as the main solvent to dissolve dry rubber and thickening materials. Gasoline mortar is used in the dipping and sizing process of the V-shaped belt wrapping layer, as well as inside and outside various rubber tubes. The bonding between the tubes and the fabric skeleton, in the process of production, use and drying, gasoline is consumed and volatilized in large quantities, which seriously pollutes the environment, endangers human health, and has fire and safety hazards, so it is not easy to store and transport; generally water-based Mucilage has no fire hazard, no pollution, easy storage, and easy transportation. However, due to poor adhesion and low bonding strength after bonding, there is no use of water-soluble mucilage in the automotive hose, oil-resistant hose and V-shaped V-belt products industry. precedent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: this water-based glue is made up of latex, dispersant, tackifier, stabilizer, accelerator, activator, vulcanizing agent, filler, anti-aging agent, compounding agent, water, and its weight formula is:

[0020] Latex 20 Dispersant 1.2 Tackifier 6.5 Stabilizer 0.001

[0021] Accelerator 0.38 Activator 0.25 Vulcanizing agent 0.4 Filler 6.1

[0022] Antiaging agent 0.13 Compounding agent 0.12 Water 64.92.

[0023] The above-mentioned latex is natural rubber and neoprene, the dispersant is BX powder, swire oil, ethylene glycol, the tackifier is coumarone, pine tar, rosin, softening resin, the stabilizer is ammonia, and the accelerator is DM, M , CZ, the active agent is zinc oxide, the vulcanizing agent is sulfur powder and zinc oxide, the filler is light calcium carbonate, the anti-aging agent is D, the compounding agent is ethyl acetate and carboxymethyl cellulose, and the water is soft water.

Embodiment 2

[0024] Embodiment 2: the weight formula of this water-based glue is:

[0025] Latex 30 Dispersant 1.5 Reinforcing resin 2.5 Tackifier 8

[0026] Stabilizer 0.001 Accelerator 0.4 Active agent 0.28 Vulcanizing agent 0.42

[0027] Filler 5 Anti-aging agent 0.15 Compounding agent 0.3 Emulsifier 0.2

[0028] Water 51.25.

[0029] The above-mentioned latex is natural rubber and neoprene, the dispersant is BX water liquid, swire oil, ethylene glycol, the reinforcing resin is phenolic resin, the tackifier is coumarone, rosin, softening resin, the stabilizer is ammonia water, and the accelerator DM and CZ, the active agent is zinc oxide, the vulcanizing agent is sulfur powder, zinc oxide, the filler is light calcium carbonate, the anti-aging agent is D, the compounding agent is carboxymethyl cellulose, ethyl acetate, emulsifier, water is soft water.

Embodiment 3

[0030] Embodiment 3: the weight formula of this water-based glue is:

[0031] Latex 45 Dispersant 1.85 Reinforced Resin 3.2 Tackifier 7

[0032] Stabilizer 0.002 Accelerator 0.42 Active agent 0.3 Vulcanizing agent 0.5

[0033] Filler 4 Anti-aging agent 0.21 Compounding agent 0.72 Emulsifier 0.33

[0034] Water 36.47.

[0035] Above-mentioned latex is natural rubber, neoprene, styrene-butadiene rubber, and dispersant is BX water liquid, swire oil, ethylene glycol, and reinforcing resin is phenolic resin, and tackifier is coumarone, rosin, softening resin, and stabilizer is Ammonia water, accelerators are DM and M, active agents are zinc oxide, vulcanizing agents are sulfur powder and zinc oxide, fillers are light calcium carbonate, anti-aging agents are D and RD, compounding agents are carboxymethyl cellulose and ethyl acetate , emulsifier, water is soft water.

[0036] Implementation 4: the weight formula of this water-based glue is:

[0037] Latex 52 Dispersant 3.4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-soluble adhesive, in particular to a multifunctional water-soluble adhesive cement for replacing a gasoline adhesive cement. The multifunctional water-soluble adhesive cement consists of latex, reinforced resin, a dispersant, a tackifier, a stabilizer, an accelerant, an activating agent, a vulcanizing agent, a filling agent, an age inhibitor, a compounding agent, an emulsifying agent and water. The multifunctional water-soluble adhesive cement provided by the invention is pollution-free, cannot cause fire hidden troubles and is easy to transport and store; when the multifunctional water-soluble adhesive cement is used for cementation between a rubber hose and V-belt wrapping cloth, the original process flow and process parameters by using the gasoline adhesive cement for cementation are not needed to be changed, technical problems do not exist on replacement, and another investment is not required; and the multifunctional water-soluble adhesive cement has the advantages of good cementing effect, high strength and long storage time and generally can be stored for more than 60 to 90 days.

Description

technical field [0001] The invention relates to an adhesive, in particular to a multifunctional water-based glue that replaces gasoline glue. Background technique [0002] my country's rubber products industry has been using gasoline and toluene as the main solvent to dissolve dry rubber and thickening materials. Gasoline mortar is used in the dipping and sizing process of the V-shaped belt wrapping layer, as well as inside and outside various rubber tubes. The bonding between the tubes and the fabric skeleton, in the process of production, use and drying, gasoline is consumed and volatilized in large quantities, which seriously pollutes the environment, endangers human health, and has fire and safety hazards, so it is not easy to store and transport; generally water-based Mucilage has no fire hazard, no pollution, easy storage, and easy transportation. However, due to poor adhesion and low bonding strength after bonding, there is no use of water-soluble mucilage in the automo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J107/00C09J111/00C09J161/10C09J11/06C09J11/04
Inventor 丁薇蔡波丁峻蔡挺
Owner 江西省新视野实业发展有限公司