A technology of decorative bricks and diatomite, which is applied in the field of decorative materials, can solve problems such as difficult construction, high requirements for construction technology, and poor hand-made fineness, and achieve the effect of simple construction and strong air humidity adjustment function
Inactive Publication Date: 2012-06-20
JILIN PROVINCE LANSHE DIATOM NEW MATERIALS
View PDF1 Cites 32 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] As a new type of environmentally friendly building material, diatom mud has been widely used in the field of decoration as a coating. At the same time, due to the complex construction process, the ...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] The formula (percentage by weight) and preparation method of embodiment 1 are as follows:
[0016] Diatomaceous earth: 20%
[0017] Gypsum powder: 67%
[0018] Vegetable fiber: 3%
[0019] Titanium dioxide: 8%
[0020] Nano Titanium Dioxide: 1%
[0021] Negative ion material: 1%
[0022] Add appropriate amount of plant pigments and water to the above formula, stir evenly to form a paste, pour it into a mold to solidify, take it out, put it in a drying box and dry it at 70°C for 11 hours.
Embodiment 2
[0024] The formula (percentage by weight) and preparation method of embodiment 2 are as follows:
[0025] Diatomaceous earth: 40%
[0026] Gypsum powder: 50%
[0027] Vegetable Fiber: 2%
[0028] Titanium dioxide: 3%
[0029] Nano Titanium Dioxide: 2%
[0030] Negative ion material: 3%
[0031] Add appropriate amount of plant pigments and water to the above formula, stir evenly to form a paste, pour it into a mold to solidify, take it out, put it in a drying box and dry it at 80°C for 12 hours.
Embodiment 3
[0033] The formula (percentage by weight) and preparation method of embodiment 3 are as follows:
[0034] Diatomaceous earth: 20.5%
[0035] Gypsum powder: 70%
[0036] Vegetable fiber: 1%
[0037] Titanium dioxide: 6%
[0038] Nano titanium dioxide: 0.5%
[0039] Negative ion material: 2%
[0040] Add appropriate amount of plant pigments and water to the above formula, stir evenly to form a paste, pour it into a mold to solidify, take it out, put it in a drying box and dry it at 90°C for 13 hours.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a decorative brick with diatomite as a main component. The decorative brick with the diatomite as the main component comprises the following components: 20-40 percent of refined diatomite, 50-70 percent of gypsum powder, 1-3 percent of plant fiber, 3-8 percent of titanium white powder, 0.5-2 percent of nano titanium dioxide and 1-3 percent of negative ion material. The decorative brick with the diatomite as the main component is made by adding a proper amount of plant pigment and water, uniformly stirring the mixture into paste, pouring the paste into a mould, solidifying and demoulding, putting into a drying box, and drying for 11-13 hours at the temperature of 70-90 DEG C. The diatomite brick has the characteristics that: the diatomite material with an air purifying function does not contain any harmful substance, has the functions of adsorbing and decomposing harmful gas, has a strong air humidity regulating function, and can be made into decorative bricks and mosaic tiles with different shapes; the transportation and the construction are simple; and the decorative bricks can be bonded onto a wall surface on site by using a special bonding agent.
Description
technical field [0001] The invention relates to a decorative material, in particular to a decorative brick mainly composed of diatomite. Background technique [0002] As a new type of environmentally friendly building material, diatom mud has been widely used in the field of decoration as a coating. At the same time, due to the complex construction process, the diatom mud coating has high requirements for construction technology, difficult construction, and poor hand-made fineness. It is not conducive to improving the popularization and development of diatom mud products. Contents of the invention [0003] The purpose of the present invention is to provide a decorative brick with diatomite as the main component. The decorative brick with diatomite as the main component expands the development direction of diatom mud and is beneficial to construction. [0004] Prescription (weight percentage) of the present invention and preparation method are as follows: [0005] Diatomi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more