Natural pullulan polysaccharide hydrogel wound dressing and preparation method thereof

A technology of pullulan polysaccharide and carboxymethylated pullulan polysaccharide, which is applied in the field of polymer biomedical materials, can solve the problems of complex synthesis process, unsatisfactory dressing, poor mechanical properties, etc., and achieve simple operation, easy acquisition, The effect of preventing dehydration

Active Publication Date: 2013-12-18
SICHUAN UNIV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such a high water vapor transmission rate will lead to complete dehydration of the wound, making the dressing stick to the wound surface and causing secondary trauma when changing
[0003] There are a large number of literature reports, the commonly used polymers synthesized by electron beam radiation cross-linking grafting technology include polyvinylpyrrolidone, polyvinyl alcohol, polyethylene oxide and polyethylene oxide, and the hydrogel wound dressings prepared by them are Although the mechanical properties are good, the swelling performance is poor, and the application in rapid hemostasis and absorption of exudate during skin healing is limited, and the synthesis process is complicated and costly
There are a large number of literature reports that although the hydrogel prepared by cross-linking natural polysaccharides has good biocompatibility, it often has poor mechanical properties and cannot meet the needs of dressings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Natural pullulan polysaccharide hydrogel wound dressing and preparation method thereof
  • Natural pullulan polysaccharide hydrogel wound dressing and preparation method thereof
  • Natural pullulan polysaccharide hydrogel wound dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The processing steps of the present embodiment are as follows:

[0037] (1) Add isopropanol to natural pullulan aqueous solution, then add sodium hydroxide aqueous solution, stir at normal pressure and 50°C until a transparent solution is formed; the natural pullulan aqueous solution is prepared with deionized water , the concentration is 0.1g / ml, and the volume ratio of the isopropanol to the natural pullulan aqueous solution is The sodium hydroxide aqueous solution is prepared with deionized water, the concentration is 0.1g / ml, the amount of the sodium hydroxide aqueous solution is limited by the molar ratio of the glucose unit of the natural pullulan polysaccharide in the mixed solution to sodium hydroxide=1:1 ;

[0038](2) Add sodium chloroacetate aqueous solution and isopropanol to the mixed solution prepared in step (1) at the same time, and react at normal pressure and 50°C for 2 hours under stirring; the concentration of the sodium chloroacetate aqueous soluti...

Embodiment 2

[0046] The processing steps of the present embodiment are as follows:

[0047] (1) Add isopropanol to natural pullulan aqueous solution, then add sodium hydroxide aqueous solution, stir at normal pressure and 70°C until a transparent solution is formed; the natural pullulan aqueous solution is prepared with deionized water , the concentration is 0.25g / ml, the volume ratio of the isopropanol to the natural pullulan aqueous solution is 1:10; the sodium hydroxide aqueous solution is prepared with deionized water, and the concentration is 0.2g / ml, and the sodium hydroxide aqueous solution The amount is limited with the mol ratio=1:1.2 of the glucose unit of natural pullulan polysaccharide and sodium hydroxide in the mixed solution;

[0048] (2) Add sodium chloroacetate aqueous solution and isopropanol to the mixed solution prepared in step (1) at the same time, and react at normal pressure and 70°C for 3 hours under stirring; the concentration of the sodium chloroacetate aqueous s...

Embodiment 3

[0056] The processing steps of the present embodiment are as follows:

[0057] (1) Add isopropanol to natural pullulan aqueous solution, then add sodium hydroxide aqueous solution, stir at normal pressure and 50°C until a transparent solution is formed; the natural pullulan aqueous solution is prepared with deionized water , the concentration is 0.3g / ml, the volume ratio of the isopropanol to the natural pullulan aqueous solution is 1:9; the sodium hydroxide aqueous solution is prepared with deionized water, and the concentration is 0.3g / ml, and the sodium hydroxide aqueous solution The amount is limited with the mol ratio=1:1.3 of the glucose unit of natural pullulan polysaccharide and sodium hydroxide in the mixed solution;

[0058] (2) Add sodium chloroacetate aqueous solution and isopropanol to the mixed solution prepared in step (1) at the same time, and react at normal pressure and 50°C for 4 hours under stirring; the concentration of the sodium chloroacetate aqueous sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a natural pullulan polysaccharide hydrogel wound dressing, which is prepared by undergoing a cross-linking reaction on a carboxy methylation pullulan polysaccharide and a hydrazine or diamine, wherein the crosslinking degree of carboxyl of the carboxy methylation pullulan polysaccharide and the hydrazine or the amino of the diamine is 30-90 percent. A preparation method of the wound dressing comprises the following steps of: performing carboxy methylation on the natural pullulan polysaccharide, preparing the carboxy methylation pullulan polysaccharide into a solution of which the concentration is 0.1-1.0g / ml by using deionized water, adding the hydrazine or diamine into the aqueous solution of the carboxy methylation pullulan polysaccharide with stirring at normal temperature and under normal pressure, adding an aqueous solution of 1-(3-dimethylamino propyl)-3-carbodiimide hydrochloride of which the concentration is 0.5-1.0g / ml after uniformly stirring, and uniformly stirring; and standing the obtained solution at normal temperature, crosslinking for at least 10 minutes, soaking into deionized water for at least 6 days after crosslinking, removing impurities, and drying in vacuum to obtain the natural pullulan polysaccharide hydrogel wound dressing.

Description

technical field [0001] The invention belongs to the field of macromolecular biomedical materials, and in particular relates to a natural pullulan hydrogel wound dressing and a preparation method thereof. Background technique [0002] Studies have shown that a humid environment is conducive to wound healing, and an appropriate water vapor transmission rate can prevent excessive dehydration of the wound. Lamke et al. (Lamke LO, Nilsson GE, Reithner HL.Burns1977;3:159–165.) reported that the water vapor transmission rates of normal skin, granulated wounds, and first-degree scald wounds were 204±12g / m 2 / day, 5138±202g / m 2 / day, 279±26g / m 2 / day. Relevant reports (Wu P, Fisher AC, Queen D, Gaylor JD.Biomaterials1995; 16:171–175.) show that it has 2000g / m 2 / day~2500g / m 2 The wound dressing with / day water vapor transmission rate can provide a moist growth environment for the wound. The water vapor transmission rates of Vigilon1 wound dressing and Geliperm1 wound dressing c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information