Steel for structural members with excellent corrosion resistance

A technology for corrosion resistance and structural components, applied in the field of steel for structural components, can solve problems such as insufficient corrosion resistance, and achieve the effect of excellent corrosion resistance

Inactive Publication Date: 2015-10-14
KOBE STEEL LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the actual situation is that none of the above technologies can be said to have sufficient corrosion resistance under severe corrosion environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for structural members with excellent corrosion resistance
  • Steel for structural members with excellent corrosion resistance
  • Steel for structural members with excellent corrosion resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The inventors of the present invention have made intensive studies in order to solve the aforementioned problems. As a result, it was found that if elements such as C, Si, Mn, P, S, Al, Cu, Ni, Cr, Ti, Ca are strictly adjusted, and the following A value obtained from the composition [(1) formula] is controlled In the range of -2.0 or more and 2.0 or less, steel materials for structural members excellent in corrosion resistance can be obtained, and the present invention has been completed.

[0018] A value = {([S] / 3)+([P] / 8)-([Mn] / 890)-([Ti] / 630)-([Ca] / 130)-([Cu] / 710 )-([Ni] / 712)-([Cr] / 330)}×10 3 …(1)

[0019] Among them, [S], [P], [Mn], [Ti], [Ca], [Cu], [Ni] and [Cr] represent S, P, Mn, Ti, Ca, Cu, Ni and Cr, respectively content (mass%).

[0020] The above-mentioned A value is a parameter showing a uniform and stable surface scale film, and is an index showing long-term corrosion resistance even in a severe corrosion environment. The coefficients corresponding to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The subject of the invention is to provide a steel material for a structural member which has excellent long term corrosion resistance even anticorrosive means such as coating or lining anticorrosion is not taken under severe corrosive environments. The steel material for a structural member satisfies specified chemical compositions and A value is between -2.0 and 2.0 as prescribed by a following forum (1). A value={([S] / 3)+([P] / 8)-([Mn] / 890)-([Ti] / 630)-([Ca] / 130)-([Cu] / 710)-([Ni] / 712)-([Cr] / 330)*103}...in(1), [S],[P],[Mn],[Ti],[Ca],[Cu],[Ni] and [Cr] respectively represent the contents (weight%) of S,P,Mn,Ti,Ca,Cu,Ni and Cr.

Description

technical field [0001] The present invention relates to steel materials for structural members that are useful as structural members of marine structures such as bridges, in addition to ships such as crude oil storage tanks, cargo ships, passenger ships, and warships, and particularly relate to exhibiting excellent corrosion resistance in severe corrosive environments Steel for structural members. In addition, the steel materials for structural members of the present invention can be applied as structural members of marine structures such as bridges in addition to various ships. Case. Background technique [0002] Steel materials used as main structural members in various ships are exposed to severe corrosive environments due to corrosive gas components, etc. in addition to salt from seawater, high temperature and high humidity, and moisture contained in crude oil. In particular, in the oil tank of the crude oil storage tank (crude oil storage tank), in addition to the vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/52C22C38/50
CPCC22C38/002C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/50C22C38/52
Inventor 小泽敬祐阪下真司吉田诚司
Owner KOBE STEEL LTD