Infrared low-emissivity coating material and preparation method thereof

A low-emissivity coating technology, applied in camouflage coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems not mentioned in the visible light band

Inactive Publication Date: 2012-08-01
UNIV OF ELECTRONICS SCI & TECH OF CHINA
View PDF10 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention is only aimed at the emissivity of the thermal infrared band, and does not mention the visible light band

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Infrared low-emissivity coating material and preparation method thereof
  • Infrared low-emissivity coating material and preparation method thereof
  • Infrared low-emissivity coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The present invention will be further described below in combination with specific embodiments.

[0036] The infrared low emissivity coating provided by the invention has a preparation process as follows:

[0037] Step 1: Prepare red paste. The red slurry is mixed with iron red, resin and solvent with an average particle size between 1 and 5 microns according to the mass ratio of 30:60:10. After being ground by a sand mill for 4 hours, an amount equivalent to iron red, resin and 0.1-0.3% anti-sedimentation agent of the total mass of the three solvents.

[0038] Step 2: Prepare yellow slurry. The yellow slurry is mixed with disazo organic yellow with an average particle size between 1 and 5 microns, resin and solvent according to the mass ratio of 30:60:10, after being ground by a sand mill for 4 hours, adding the equivalent of bis The anti-sedimentation agent is made of 0.1-0.3% of the total mass of azo organic yellow, resin and solvent.

[0039]Step 3: Prepare the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to view more

Abstract

An infrared low-emissivity coating material and a preparation method thereof belong to the technical field of functional materials. The infrared low-emissivity coating material comprises the following components by weight: 0.8 to 1 part of red slurry, 2 to 4 parts of yellow slurry, 1 to 3 parts of dispersing slurry of sheet aluminium powder, 35 to 37 parts of dispersing slurry of sheet aluminium powder coated with silicon dioxide or ferric oxide, 50 to 58 parts of solvent, 3 to 5 parts of curing agent and 0.1 to 0.3 part of flatting agent. The infrared low-emissivity coating material provided by the invention can simulate the spectral reflection curve of the northern ocher background, wherein a near infrared band has higher solar reflectivity, the average emissivity of a thermal infrared band of 3 to 5 Mum is lower than 0.35, and the average emissivity of a thermal infrared band of 8 to 14 Mum is lower than 0.45; and industrial production can be achieved.

Description

technical field [0001] The invention belongs to the technical field of functional materials, and relates to an energy-saving and environment-friendly architectural decoration coating, an infrared low-emissivity coating for infrared camouflage and a preparation method. Background technique [0002] With the rapid development of industrial production, the energy problem has increasingly become a prominent contradiction that plagues social and economic development. Therefore, while emphasizing the improvement of productivity, people are paying more and more attention to the issue of energy consumption. Energy conservation and consumption reduction, energy conservation and environmental protection, energy efficiency ratio, etc. have become social hot words, and various technologies to improve energy efficiency have also become hot technologies. [0003] Optical studies have shown that the more reflective an opaque object, the lower the emissivity. Therefore, under visible light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C09D5/30
Inventor 翁小龙朱彬袁乐
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap