Method for dyeing conductive polyester fiber

A polyester fiber and dyeing method technology, applied in the field of dyeing, can solve the problems of the dye uptake rate of color difference, not high enough, less research on conductive fibers and fabric dyeing processes, etc., so as to retain the conductive effect, improve the dye uptake rate and color fastness. , reduce the effect of antistatic properties

Active Publication Date: 2014-03-26
TAICANG RONGWEN SYNTHETIC FIBER
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two fabrics are different from conventional polyester fibers because the fabrics have multiple components, and each component has a different dye absorption rate, which is prone to color difference and insufficient dyeing rate. At present, there are few researches on the dyeing process of conductive fibers and fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A conductive polyester fiber dyeing process mainly includes the following steps: desizing→alkali weight reduction→dyeing→reduction cleaning.

[0019] In the desizing process, a sodium carbonate solution with a mass concentration of 0.2% is prepared, and detergent 209 is added to make the concentration 0.5%, the bath ratio is 1:30, the desizing temperature is 100 degrees, and after 60 minutes of desizing , take out the conductive fiber fabric and put it into the alkali weight reduction tank. The solution formula in the alkali reduction vat is: sodium hydroxide with a mass concentration of 3%, accelerator SN with a mass concentration of 0.1%; the liquor ratio is 1:30, the treatment temperature is 100 degrees, and after 30 minutes of treatment, it is put into the dyeing vat dyeing in. The solution ratio in the dyeing vat is: disperse blue SF-G with a mass concentration of 5%; ammonium sulfate with a mass concentration of 0.2%; dispersant NNO with a mass concentration of 0...

Embodiment 2

[0022] In the desizing process, a sodium carbonate solution with a mass concentration of 0.4% is prepared, and detergent 201 is added to make the concentration 0.8%, the bath ratio is 1:25, the desizing temperature is 90 degrees, and after 40 minutes of desizing , take out the conductive fiber fabric and put it into the alkali weight reduction tank. The formula of the solution in the alkali reduction vat is: sodium hydroxide with a mass concentration of 1%, accelerator SN with a mass concentration of 0.3%; the liquor ratio is 1:25, and the treatment temperature is 120 degrees. After 10 minutes of treatment, put it into the dyeing vat dyeing in. The solution ratio in the dyeing vat is: disperse blue SF-G with a mass concentration of 3%; disperse yellow UN-SE with a mass concentration of 2%, ammonium sulfate with a mass concentration of 0.4%; dispersant NNO with a mass concentration of 0.4%, The pH value of the solution is 4.0, and the dyeing temperature is 100 degrees. After 3...

Embodiment 3

[0024] In the desizing process, a sodium carbonate solution with a mass concentration of 0.3% is prepared, and detergent 209 is added to make the concentration 0.6%, the bath ratio is 1:25, the desizing temperature is 95 degrees, and after 50 minutes of desizing , take out the conductive fiber fabric and put it into the alkali weight reduction tank. The formula of the solution in the alkali reduction vat is: sodium hydroxide with a mass concentration of 5%, accelerator SN with a mass concentration of 0.2%; the bath ratio is 1:25, the treatment temperature is 70 degrees, and after 70 minutes of treatment, it is put into the dyeing vat dyeing in. The solution ratio in the dyeing vat is: disperse yellow UN-SE with a mass concentration of 10%, ammonium sulfate with a mass concentration of 0.1%; dispersant NNO with a mass concentration of 0.3%, the pH value of the solution is 4.5, and the dyeing temperature is 80 degrees. After 40 minutes of staining, enter the reduction wash. Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for dyeing conductive polyester fibers, mainly comprising the following steps of: desizing the conductive polyester fibers with desizing solution; carrying out alkali reducing treatment on the desized conductive polyester fibers in alkali reducing solution; dyeing the conductive polyester fibers, which is subjected to the alkali reducing treatment, in dyeing solution; carrying out reduction clearing treatment on the dyed conductive polyester fibers in reduction clearing solution; and taking out and drying the conductive polyester fibers. By adopting the dyeing method provided by the invention, a dyeing technological process and parameters are optimized, influence of dyeing and finishing processes on antistatic property, rate of dye-uptake, colour fastness and handfeel of the conductive polyester fibers and fabric is reduced, conductive effect of the fabric is maintained to the utmost extent, and the rate of dye-uptake of dye and colour fastness are improved.

Description

technical field [0001] The invention relates to a dyeing method, in particular to a dyeing method of conductive polyester fiber. Background technique [0002] Polyester fiber fabrics have poor hygroscopicity, are extremely prone to static electricity, and are difficult to dissipate, which directly affects the production, processing and application of polyester fabric textiles, and even causes serious static electricity disasters. At home and abroad, a lot of research has been done on eliminating the static electricity of polyester fibers and their fabrics, and the preparation of conductive fibers and fabrics. The common method is to prepare conductive fibers by blending, add conductive agents to polyester chips, and obtain conductive fibers by melt spinning; Another method is to mix and weave polyester fiber and conductive metal wire to obtain a metal-wire-containing fabric, and the entire fabric has conductive properties due to the conductive effect of the metal wire. Thes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06P3/52D06P3/54D06P1/16D06P1/673D06P5/02D06P5/10D06L1/14D06M11/38D06M101/32
Inventor 全潇
Owner TAICANG RONGWEN SYNTHETIC FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap