Dry forsterite sand for full-mold casting and preparation method for dry forsterite sand

A technology of forsterite sand and forsterite, which is applied in the field of new filled dry sand for full mold casting, which can solve the problems of forsterite alkaline, narrow application area, insufficient flow filling of artificial forsterite sand, etc. , to achieve good reusability, promote development, and prevent silicosis

Active Publication Date: 2012-09-19
湖北镁兴科技股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a full mold casting forsterite dry sand and its preparation method, which can improve the artificial forsterite sand’s insufficient flow filling and forsterite’s partial alkalinity, and is only suitable for alkaline high-alloy The production of steel castings, the defect that the application surface is too narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Take 60kg of 20-mesh forsterite sand, 36kg of 30-mesh forsterite sand, 3kg of graphite powder, 2 kg of organic resin, dry mix for 20 minutes, add 8kg of tap water for wet grinding for 20 minutes, and then dry (water content ≤ 1% ), and then sieved, and the product of 10 mesh to 30 mesh was packaged and put into storage to obtain the dry forsterite sand for solid mold casting.

Embodiment 2

[0018] Take 20 mesh forsterite sand 50kg, 30 mesh forsterite sand 30kg graphite powder 2kg, organic resin 3 kg, dry mix for 20 minutes, add tap water 8kg wet grinding for 20 minutes, then dry (water content ≤ 1% ), and then screened, packaged and put into storage to obtain forsterite dry sand for solid mold casting.

Embodiment 3

[0020] Take 20-mesh forsterite sand 40kg, 30-mesh forsterite sand 45kg graphite powder 3kg, organic resin 3kg, dry mix for 20 minutes, add tap water 8kg wet grinding for 20 minutes, then dry (water content ≤ 1% ), and then screened, packaged and put into storage to obtain forsterite dry sand for solid mold casting.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses dry forsterite sand for full-mould casting and a preparation method for the dry forsterite sand. The dry forsterite sand is prepared from the following raw materials in part by weight: 80 to 96 parts of forsterite sand, 2 to 3 parts of graphite powder and 1 to 3 parts of organic resin. The preparation method comprises the following steps of: mixing the forsterite sand, the graphite powder and the organic resin in a proportion, preblending, dry-mixing, adding tap water for wet mixed milling, drying and sieving to obtain the dry forsterite sand for the full-mould casting. The dry forsterite sand for the full-mould casting can overcome the defects that the flowability and the filling property of artificial forsterite sand are insufficient, the forsterite sand is slightly alkaline and is only applicable to the production of alkaline high-alloy steel castings, and the application range is too narrow, and promotes the development of full-mold casting industry.

Description

technical field [0001] The invention relates to a filling dry sand for full mold casting, in particular to a new filling dry sand special for full mold casting which is coated and denatured on forsterite sand. Background technique [0002] Generally, forsterite sand is artificial sand, which is triangular or polygonal, with poor flow filling performance, and forsterite sand is alkaline, and its application area is narrow. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a full mold casting forsterite dry sand and its preparation method, which can improve the artificial forsterite sand’s insufficient flow filling and forsterite’s partial alkalinity, and is only suitable for alkaline high-alloy In the production of steel castings, the application surface is too narrow. [0004] In order to solve the above-mentioned technical problems, the technical solution adopted in the present invention is: a kind of full mold c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B14/06
Inventor 韩晶高申明
Owner 湖北镁兴科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com