Polymer modified emulsified asphalt composition and preparation method thereof

A technology of emulsified asphalt and composition, which is applied in the field of cationic emulsified petroleum asphalt building waterproof material composition and its preparation, can solve the problems of operator influence, long drying process, external force damage, etc., achieve high elongation at break, improve Anti-corrosion and permeability-enhancing effects

Active Publication Date: 2012-09-19
SHANXI MINGKESI TECH
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this waterproof coating is a solvent-based coating, which is inconvenient to use and will have a certain impact on operators.
[0008] The publication number is 102079903A, which discloses a "water-based waterproof coating", which uses natural latex, styrene-acrylic latex, dibutyltin dilaurate curing agent, trieth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer modified emulsified asphalt composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0033] Implement the preparation method of the polymer modified emulsified asphalt composition of the present invention, its composition and mass content parts are as follows:

[0034] Component A: 46 parts of emulsified petroleum asphalt, 22 parts of neoprene latex, 9 parts of styrene-butadiene latex, 4 parts of acrylate latex, 6 parts of epoxy resin emulsion, 5 parts of dioctyl phthalate, tetradecyl di 0.5 parts of methyl ammonium chloride emulsifier, 0.5 parts of BYK-8821 defoamer, 7.0 parts of deionized water; the emulsifier tetradecyl dimethyl ammonium chloride in the above materials was stirred and dissolved in After deionized water, then add the plasticizer dioctyl phthalate to stir and emulsify, and then stir and mix with other components at room temperature to obtain component A of the polymer asphalt emulsion.

[0035] Component B: 20 ​​parts of industrial ethanol, 6 parts of industrial ethylene glycol, 5 parts of sodium hydroxide, 7 parts of water-based epoxy resin ...

specific Embodiment approach 2

[0037] Implement the preparation method of the polymer modified emulsified asphalt composition of the present invention, its composition and mass content parts are as follows:

[0038] Component A: 50 parts of emulsified petroleum asphalt, 20 parts of neoprene latex, 5 parts of styrene-butadiene latex, 3 parts of acrylic latex, 4 parts of epoxy resin emulsion, 4 parts of dioctyl phthalate, cetyl di 0.3 parts of methyl benzyl ammonium chloride emulsifier, 0.4 parts of BYK-8821 defoamer, 13.3 parts of deionized water; After stirring and dissolving in deionized water, then adding the plasticizer dioctyl phthalate to stir and emulsify, and then stirring and mixing with other components at room temperature to obtain component A of the polymer asphalt emulsion.

[0039] Component B: 30 parts of industrial ethanol, 4 parts of industrial ethylene glycol, 4 parts of sodium hydroxide, 5 parts of water-based epoxy resin curing agent, 57 parts of industrial water; dissolve the sodium hydr...

specific Embodiment approach 3

[0041] Implement the preparation method of the polymer modified emulsified asphalt composition of the present invention, its composition and mass content parts are as follows:

[0042] Component A: 56 parts of emulsified petroleum asphalt, 17 parts of neoprene latex, 4 parts of styrene-butadiene latex, 1 part of acrylic latex, 3 parts of epoxy resin emulsion, 3 parts of dioctyl phthalate, 3 parts of octadecyl tri 0.2 parts of methyl ammonium chloride emulsifier, 0.3 parts of BYK-8821 defoamer, 15.5 parts of deionized water; the emulsifier octadecyl trimethyl ammonium chloride in the above materials was stirred and dissolved in After deionized water, then add the plasticizer dioctyl phthalate to stir and emulsify, and then stir and mix with other components at room temperature to obtain component A of the polymer asphalt emulsion.

[0043] Component B: 35 parts of industrial ethanol, 2 parts of industrial ethylene glycol, 3 parts of sodium hydroxide, 4 parts of water-based epox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tear strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polymer modified emulsified asphalt composition and a preparation method thereof, wherein the component A of the polymer modified emulsified asphalt composition comprises cationic-type emulsified petroleum asphalt, cationic-type neoprene latex, non-ionic-type epoxy resin emulsion and additives; the B component of the polymer modified emulsified asphalt composition comprises industrial alcohol, a waterborne epoxy resin curing agent and industrial water. When the components A and B are sprayed on the surface of a sprayed object at the same time, the components A and B are rapidly settled and cured to form a polymer asphalt water-proof glue film layer; the various large molecules in the glue film layer interact to form a semi-interpenetrating network structure; under the synergistic effect of the additives, the water-proof material glue film has the characteristics of favorable weather resistance, adhering force, stretching intensity, elongation rate, water resistance, seepage resistance, dampness resistance, corrosion resistance and the like, and the polymer modified emulsified asphalt composition can be widely applied to the fields of water resistance and dampness resistance of medicine and gun powder warehouse, as well as the direct water resistance, seepage resistance, corrosion resistance and the like of metal roofing.

Description

technical field [0001] The invention relates to an emulsified asphalt composition and a preparation method thereof, in particular to a polymer-modified cationic emulsified petroleum asphalt building waterproof material composition and a preparation method thereof. The waterproof material formed by the composition can be widely used in the fields of civil buildings, tunnels, dams, garbage landfills, anti-leakage, moisture-proof warehouses and the like. technical background [0002] Waterproof material is a kind of building material chemical products involving thousands of households. Usually, this material is in the form of viscous liquid or solid powder with no fixed shape at room temperature to form a paste with water. Through the volatilization of solvent or water volatilization or reaction After curing, a tough film layer is formed to achieve the purpose of waterproof and anti-seepage. At present, waterproof materials are mainly divided into two categories: solvent-based...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L11/02C08L9/08C08L33/04C08L63/02C08K5/12C08K5/053C09D195/00C09D111/02C09D109/08C09D163/02C09D7/12
Inventor 苏红印宋纪明李祥云
Owner SHANXI MINGKESI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap