Hydrophobic glass glaze

A glass glaze and hydrophobic technology, applied in the field of ceramic glaze, can solve the problems of poor hydrophobic performance and easy breeding of bacteria, and achieve good waterproof and moisture-proof performance, and the effect of scientific and reasonable proportioning

Inactive Publication Date: 2013-11-06
CARLOBBIA GLAZE KUNSHAN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glaze has been widely used in people's daily life because of its good smoothness, but the hydrophobicity of the glaze surface in the prior art is relatively poor, and it is easy to occupy a large amount of water on the glaze surface after washing, and it is easy to breed bacteria when it is wet. To prepare the glaze for the surface of the basin in the bathroom or kitchen, it needs to have strong hydrophobicity, so that it is not easy to form water droplets on the surface after washing. Therefore, it is necessary to develop and design a kind of glaze with good hydrophobicity water-based glass glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of glass glaze with hydrophobicity, it is made of the raw material of following parts by weight:

[0017] 40 parts of silicate, 30 parts of aluminum nitride, CaCO 3 15 parts, BaSO 4 10 parts, ZnSO 4 15 parts, chromium oxide 20 parts, acrylic resin 15 parts, triglycidyl isocyanurate 12 parts.

Embodiment 2

[0019] A kind of glass glaze with hydrophobicity, it is made of the raw material of following parts by weight:

[0020] 30 parts of silicate, 10 parts of aluminum nitride, CaCO 3 5 parts, BaSO 4 5 parts, ZnSO 4 5 parts, chromium oxide 10 parts, acrylic resin 5 parts, triglycidyl isocyanurate 3 parts.

Embodiment 3

[0022] A kind of glass glaze with hydrophobicity, it is made of the raw material of following parts by weight:

[0023] 35 parts of silicate, 20 parts of aluminum nitride, CaCO 3 10 parts, BaSO 4 8 parts, ZnSO 4 10 parts, chromium oxide 15 parts, acrylic resin 10 parts, triglycidyl isocyanurate 10 parts.

[0024] The water-repellent glass glaze provided by the present invention ball-mills each solid component into 40-60 meshes, fires at a high temperature of 1100-1200°C for 30 minutes, sprays additives when the temperature drops to 300-400°C, and cools to room temperature get.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a hydrophobic glass glaze, which is prepared from the following raw materials, by weight, 30-40 parts of a silicate, 10-30 parts of aluminum nitride, 5-15 parts of CaCO3, 5-10 parts of BaSO4, 5-15 parts of ZnSO4, 10-20 parts of chromium oxide, 5-15 parts of acrylic resin, and 3-12 parts of an assistant agent. The hydrophobic glass glaze of the present invention has characteristics of smooth glaze, fineness, excellent hand feeling, and good hydrophobicity. With the hydrophobic glass glaze of the present invention, water can be well prevented from gathering on the glaze, and the glaze can maintain the dry state, such that good water resistance and good dampness resistance are provided. In addition, the glass glaze of the present invention can be widely used in preparations of bathtubs in bathrooms and kitchens.

Description

technical field [0001] The invention relates to a ceramic glaze, in particular to a hydrophobic glass glaze. Background technique [0002] Glaze has been widely used in people's daily life because of its good smoothness, but the hydrophobicity of the glaze surface in the prior art is relatively poor, and it is easy to occupy a large amount of water on the glaze surface after washing, and it is easy to breed bacteria when it is wet. To prepare the glaze for the surface of the basin in the bathroom or kitchen, it needs to have strong hydrophobicity, so that it is not easy to form water droplets on the surface after washing. Therefore, it is necessary to develop and design a kind of glaze with good hydrophobicity Water-based glass glaze. Contents of the invention [0003] Purpose of the invention: The technical problem to be solved by the present invention is to overcome the deficiencies of the prior art and provide a glass glaze with good surface smoothness, good hydrophobi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 赵白弟
Owner CARLOBBIA GLAZE KUNSHAN