Nanometal bonding agent and polycrystal CBN (cubic boron nitride) composite sheet made by using same

A technology of nano-metal and binder, applied in the field of polycrystalline CBN composite sheets, to achieve the effect of increasing volume ratio, good sintering promotion and prolonging service life

Inactive Publication Date: 2012-11-28
ZHONGNAN DIAMOND CO LTD
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the limitations of the formula and process of domestic PCBN products, there are problems: 1) The wear ratio of the composite sheet is 4000-6000 (foreign is about 8000-10,000)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A polycrystalline CBN composite sheet made of a nano-metal bond, comprising a CBN polycrystalline layer and a hard alloy substrate, wherein the CBN polycrystalline layer is composed of the following raw materials in weight percent: CBN powder (1- 3μm) 55% and nano-metal bond 45%, the cemented carbide substrate is composed of the following raw materials in weight percentage: WC powder (1.6-2.2μm) 87.5-88.5% and analytically pure cobalt powder (1-1.2μm ) 11.5% to 12.5%; the nano-metal binder is composed of the following raw materials in weight percentage: analytically pure TiN powder (8-12nm) 40%, analytically pure TiC powder (8-12nm) 20%, analytically pure Si 3 N 4 Co powder (8-12nm) 15%, analytically pure Co powder (22-36nm) 15% and analytically pure Al powder (22-36nm) 10%.

[0023] The preparation method of above-mentioned polycrystalline CBN composite sheet, it comprises the steps:

[0024] 1) Purification and reduction treatment: Boil CBN powder with 30% sodium h...

Embodiment 2

[0030] A polycrystalline CBN composite sheet made of a nano-metal bond, comprising a CBN polycrystalline layer and a hard alloy substrate, wherein the CBN polycrystalline layer is composed of the following raw materials in weight percent: CBN powder (1- 3μm) 95% and nano-metal bond 5%, the cemented carbide substrate is composed of the following raw materials in weight percentage: WC powder (1.6-2.2μm) 87.5% ~ 88.5% and analytically pure cobalt powder (1-1.2 μm) 11.5% to 12.5%; the nano-metal binder is composed of the following raw materials in weight percentage: analytically pure TiN powder (8-12nm) 35%, analytically pure TiC powder (8-12nm) 20%, analytically pure TiC powder (8-12nm) Pure Si 3 N 4 Co powder (8-12nm) 15%, analytically pure Co powder (22-36nm) 15% and analytically pure Al powder (22-36nm) 15%.

[0031] The preparation method of the polycrystalline CBN composite sheet is the same as in Example 1; its main performance indicators: 1) The wear ratio of the composite...

Embodiment 3

[0033] A polycrystalline CBN composite sheet made of a nano-metal bond, comprising a CBN polycrystalline layer and a hard alloy substrate, wherein the CBN polycrystalline layer is composed of the following raw materials in weight percent: CBN powder (1- 3μm) 60% and nano-metal bond 40%, the cemented carbide substrate is composed of the following raw materials in weight percentage: WC powder (1.6-2.2μm) 87.5-88.5% and analytically pure cobalt powder (1-1.2μm ) 11.5-12.5%; the nano-metal binder is composed of the following raw materials in weight percentage: 37% of analytically pure TiN powder (8-12nm), 23% of analytically pure TiC powder (8-12nm), 23% of analytically pure Si 3 N 4 Co powder (8-12nm) 15%, analytically pure Co powder (22-36nm) 15% and analytically pure Al powder (22-36nm) 10%.

[0034] The preparation method of the polycrystalline CBN composite sheet is the same as in Example 1; its main performance indicators: 1) The wear ratio of the composite sheet is 86 mill...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a nanometal bonding agent. The bonding agent consists of the following raw materials in percentage by weight: 35-40% of TiN powder, 20-25% of TiC powder, 15-20% of Si3N4 powder, 15-20% of Co powder and 10-20% of Al powder. The invention also discloses a polycrystal CBN (cubic boron nitride) composite sheet made by using the nanometal bonding agent. The polycrystal CBN composite sheet comprises a CBN polycrystal layer and a hard alloy substrate, wherein the CBN polycrystal layer consists of the following raw materials in percentage by weight: 55-95% of CBN powder and 5-45% of nanometal bonding agent. In the polycrystal CBN composite sheet provided by the invention, by adopting the nanometal bonding agent in the formula of polycrystal layer, the technical bottleneck in high impact toughness and high bending strength of a PCBN composite sheet is broken, the impact resistance of a tool is enhanced, and the service life of the tool is prolonged.

Description

Technical field [0001] The present invention belongs to the field of cubic nitrogen boron and hard alloy composite tool materials. It involves a polycrystal CBN composite tablets made of nano metal binding agent and the use of this binding agent.Half -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -semi -seductives are the same. Background technique [0002] Polycrystalline cubic boron nitride composite (PCBN) material has high hardness and abrasion resistance, high thermal stability and high temperature hardness, excellent chemical properties.The polychen cubic boron nitride compound was successfully developed in the last century by the United States GE company.Due to better stability, thermal conductivity and lower friction coefficient, PCBN is more and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F7/06
Inventor 卢灿华张涛刘俊涛窦明
Owner ZHONGNAN DIAMOND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap