Production method of tape-casting glazed ceramic vase

A production method and ceramic technology, applied in the field of ceramics, can solve problems such as failure to attract consumers and lack of novelty, and achieve the effect of natural and random appearance, breakthrough design style, and unique and novel aesthetic feeling

Inactive Publication Date: 2013-01-23
李永强
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the traditional vases are decorated with decals or painted on the surface, the style is simple and traditional, lacks new ideas, and cannot attract consumers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through examples.

[0010] Take 10 parts by weight of spodumene, 12 parts by weight of quartz, 44 parts by weight of feldspar, 18 parts by weight of calcium carbonate, 20 parts by weight of talc, and 5 parts by weight of kaolin and put them into a ball mill, and then add 30% of the mixed raw materials into clear water for ball milling Go through a 240 mesh sieve to make enamel for subsequent use;

[0011] According to the traditional production method of ceramic products, a 100cm high ceramic vase body is produced;

[0012] Spray the above-mentioned spare enamel evenly on the surface from the mouth of the ceramic vase carcass to the middle of the bottle body in 25 seconds, the thickness of the glaze layer is 2mm, then put it in the kiln, and fire it at 130°C for 12 minutes at low temperature , and then heated up to 1110 ° C for 5 hours to make the product.

[0013] There are many streamlined glazes on the surface...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a tape-casting glazed ceramic vase. The production method is characterized by comprising the following production steps of: (1) taking and putting triphane, quartz, feldspar, calcium carbonate, steatite and kaolin in a ball mill, and then, adding clear water to carry out ball milling and sieving to prepare a ceramic glaze for later use; (2) producing a ceramic vase biscuit with a height of 60-120 cm; and (3) uniformly coating the ceramic glaze for later use on a surface in a spray coating way from a vase neck of the ceramic vase biscuit to the middle part of a vase body within 20-30 seconds to form a glaze layer which has a thickness of 1-2 mm, then placing the ceramic vase biscuit in a kiln, firstly carrying out low-temperature sintering for 10-15 minutes at 120-140 DEG C, and then, heating to 1100-1120 DEG C for sintering for 4-5 hours so as to prepare a finished product. The tape-casting glaze is formed on the surface of the vase produced by the invention; the vase has natural and random appearance; a unique and novel aesthetic feeling is generated; and the design style of the conventional product is broken through.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a production method of cast glazed ceramic vases. Background technique [0002] Traditional vases are mostly decorated with decals or colored paintings on their surfaces. The style is simple and traditional, lacking in novelty, and unable to attract consumers. Contents of the invention [0003] In order to overcome the above disadvantages, the present invention provides a production method of cast glazed ceramic vases. [0004] The production method of casting shape glazed ceramic vase of the present invention is characterized in that, comprises the following production steps: [0005] (1) Put 10 parts by weight of spodumene, 12 parts by weight of quartz, 44 parts by weight of feldspar, 18 parts by weight of calcium carbonate, 20 parts by weight of talc, and 5 parts by weight of kaolin into a ball mill, and then add 30% of the mixed raw materials The clear water of ball milling is cr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 李永强
Owner 李永强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products