A technology of pure titanium and coils, applied in the direction of manufacturing tools, welding equipment, metal rolling, etc., can solve the problems of lack of large-scale promotion and application, slow development of titanium welded pipes, etc., and achieve the elimination of camber phenomenon and the quality of welds Excellent, guaranteed uniform effect

Inactive Publication Date: 2013-02-06
WESTERN TITANIUM TECH
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The price level of pure titanium coil raw materials imported from abroad is almost equivalent to the price of domestic titanium welded pipe products, which makes the development of the entire domestic titanium welded pipe market slow and cannot be widely used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method of wide-width pure titanium roll
  • Preparing method of wide-width pure titanium roll
  • Preparing method of wide-width pure titanium roll

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of the wide-width pure titanium coil of the present embodiment comprises the following steps:

[0027] Step 1. The TA1 pure titanium slab with a thickness of 5mm, a width of 1560mm, and a length of 10m is subjected to atmospheric annealing treatment, and after cooling in the furnace, pickling removes the surface scale; the temperature of the atmospheric annealing treatment is 650°C, and the atmospheric annealing The processing time is 15 minutes;

[0028] Step 2: Plasma weld 20 pure titanium slabs after pickling in step 1 with a plasma welder to obtain a pure titanium welded slab with a width of 1560 mm and a length of 200 m, and then use a winder to weld the pure titanium slabs The welded slab is wound up to obtain a pure titanium coil; the current of the plasma welding is 185A, and the speed of the plasma welding is 330mm / min;

[0029] Step 3. Use the 1780mm six-high reversing cold rolling mill produced by Antai Technology Co., Ltd. to carry ou...

Embodiment 2

[0036] The preparation method of the wide-width pure titanium coil of the present embodiment comprises the following steps:

[0037] Step 1. The TA2 pure titanium slab with a thickness of 2 mm, a width of 1400 mm, and a length of 9.5 m is subjected to atmospheric annealing treatment, and after cooling in the furnace, pickling removes the surface scale; the temperature of the atmospheric annealing treatment is 680 ° C, the atmosphere The annealing time is 10min;

[0038]Step 2: Plasma weld 14 pure titanium slabs after pickling in step 1 by plasma welding machine to obtain a pure titanium welded slab with a width of 1400 mm and a length of 133 m, and then use a winder to weld the pure titanium slabs The welded slab is wound up to obtain a pure titanium coil; the plasma welding current is 160A, and the plasma welding speed is 300mm / min;

[0039] Step 3. Use the 1780mm six-high reversing cold rolling mill produced by Antai Technology Co., Ltd. to carry out 15 passes of rolling on...

Embodiment 3

[0046] The preparation method of the wide-width pure titanium coil of the present embodiment comprises the following steps:

[0047] Step 1. The TA1 pure titanium slab with a thickness of 1 mm, a width of 1250 mm, and a length of 9.8 m is subjected to atmospheric annealing treatment, and after cooling in the furnace, pickling removes the surface scale; the temperature of the atmospheric annealing treatment is 650 ° C, the atmosphere The annealing time is 20min;

[0048] Step 2: Plasma weld 18 pure titanium slabs after pickling in step 1 by plasma welding machine to obtain a pure titanium welded slab with a width of 1250 mm and a length of 176.4 m, and then use a winder to wind the pure titanium slabs The titanium welding slab is rolled up to obtain a pure titanium coil; the current of the plasma welding is 250A, and the plasma welding speed is 350mm / min;

[0049] Step 3. Use the 1780mm six-high reversing cold rolling mill produced by Antai Technology Co., Ltd. to carry out 16...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparing method of a wide-width pure titanium roll. The preparing method includes the following steps: 1 pure titanium slabs with a certain specification are subjected to annealing in the air and acid-washing; 2 10-20 acid-washed pure titanium slabs are welded to form a roll to obtain a pure titanium coiled slab; 3 a 1780mm six-roller reversing cold mill is adopted to roll the pure titanium coiled slab to obtain a pure titanium rolled coiled slab; and 4 the pure titanium rolled coiled slab is sequentially subjected to oil removing, annealing, flattening and shearing to obtain the wide-width pure titanium roll with thickness to be 0.5-3.0mm and the width to be 1000-1500mm. The preparing method is simple in process and simple and convenient to operate, needs no special or complex devices, and can achieve large-scale industrial production by aid of conventional devices. The wide-width pure titanium roll prepared in the method fills the gap in domestic pure titanium roll products, breaks through technique blockade of foreign pure titanium roll products, shortens the gap of domestic technology and the international advanced technology, and powerfully promotes pure titanium material development.

Description

technical field [0001] The invention belongs to the technical field of metal material processing, and in particular relates to a preparation method of a wide-width pure titanium coil. Background technique [0002] Pure titanium coils are widely used in aviation, aerospace, nuclear power plants, chemical industry, construction and other fields. Its products include thin titanium plates for heat exchangers, titanium plates for composite plates, titanium plates for welded pipes, titanium plates for construction, etc. At present, several sets of titanium tube welding production lines have been built in China, but the upstream product of titanium tube production, pure titanium coil, mainly relies on imports from abroad. The price level of pure titanium coil raw materials imported from abroad is almost equivalent to the price of domestic titanium welded pipe products, which makes the development of the entire domestic titanium welded pipe market slow and cannot be widely used. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/02B23K10/02B21B1/36C22F1/18C21D8/02
Inventor 戴毅李辉吕利强吴晓东王兴刘宇明邢义胜赵福军宋建华周高玉侯高洁王娟王军刚舒滢张清杨建朝
Owner WESTERN TITANIUM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap