Welding material for ni-based heat-resistant alloy, and welded metal and welded joint each using same

A technology of heat-resistant alloys and welding materials, applied in the direction of welding/welding/cutting articles, welding/cutting media/materials, welding media, etc., can solve problems such as relaxation cracks and stress relaxation cracks that do not consider stress relaxation

Inactive Publication Date: 2013-02-27
NIPPON STEEL CORP
View PDF15 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the above-mentioned Patent Documents 6 to 8, stress relaxation relaxation cracks are not considered at all.
Therefore, the weld metal obtained by using the welding materials proposed in Patent Document 6 to Patent Document 8 also has a problem about stress relaxation cracking.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding material for ni-based heat-resistant alloy, and welded metal and welded joint each using same
  • Welding material for ni-based heat-resistant alloy, and welded metal and welded joint each using same
  • Welding material for ni-based heat-resistant alloy, and welded metal and welded joint each using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0133] The ingot is melted and cast in the laboratory with the chemical composition shown in Table 1, and is made into a plate with a thickness of 12mm, a width of 50mm, and a length of 100mm through hot forging, hot rolling, heat treatment and mechanical processing. The plate is used as the plate for welding base material.

[0134] In addition, the ingots obtained by melting and casting the materials of symbols 1 to 6 having the chemical compositions shown in Table 2 were produced by hot forging, hot rolling, and mechanical processing to have an outer diameter of 1.2 mm and a length of 1000mm of welding material (welding wire).

[0135] Table 1

[0136] Table 1

[0137]

[0138] Table 2

[0139]

[0140] In the length direction of the above-mentioned plate for welding the base metal, a V-shaped groove with an angle of 30° and a thickness of the blunt edge of 1 mm is processed, and then "DNiCrFe-3" specified in JIS Z3224 (1999) is used as an electrode, Constraint...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

Disclosed is a welding material for an Ni-based heat-resistant alloy, which has a chemical composition that contains 0.06-0.18% of C, 0.5% or less of Si, 1.5% or less of Mn, 46-56% of Ni, 10-15% of Co, 20-25% of Cr, more than 10.0% but 14.0% or less of Mo, 0.01-0.5% of Ti, 0.1-1.0% of Al and 0.006% or less of N, and additionally if necessary, 0.1% or less of Nd with the balance made up of Fe and impurities, while controlling O, P and S contained as impurities to 0.02% or less, 0.008% or less, and 0.005% or less, respectively. The welding material for an Ni-based heat-resistant alloy exhibits excellent high-temperature cracking resistance during the welding. A welded metal that has high-temperature cracking resistance during the welding, stress relaxation cracking resistance when in use for a long period of time at high temperatures, and good creep strength can be provided using the above-described welding material. In addition, a welded joint can be provided using the above-described welding material, said welded joint being composed of a base of an Ni-based heat-resistant alloy that has excellent high-temperature strength and a welded metal that has high-temperature cracking resistance during the welding, stress relaxation cracking resistance when in use for a long period of time at high temperatures, and good creep strength.

Description

technical field [0001] The present invention relates to a welding material for a Ni-based heat-resistant alloy, a weld metal and a welded joint using the welding material. Specifically, it relates to a welding material suitable for welding Ni-based heat-resistant alloys used in equipment used at high temperatures, such as boilers for power generation, and weld metals and welded joints obtained by using the welding materials. Ni-based heat-resistant alloys in. Background technique [0002] In recent years, from the viewpoint of reducing the environmental load, the operating conditions of power generation boilers and the like have been increased to high temperature and high pressure globally, and materials used in power generation boilers and the like have been required to have better high-temperature strength. [0003] As a material satisfying such requirements, there is, for example, a Ni-based heat-resistant alloy specified in UNS 06617. In addition, Patent Document 1 to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30C22C19/05
CPCB23K35/3033B23K2203/08C22C19/055B23K2103/26
Inventor 平田弘征吉泽满小川和博伊势田敦朗仙波润之
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap