High-carbon and low-alloy steel wire rod for producing fine steel wires, and its manufacturing method
A technology of low-alloy steel and thin steel wire, applied in the field of low-alloy high-carbon steel, can solve problems such as unfavorable cost reduction and complex alloy composition
Active Publication Date: 2013-03-06
ANGANG STEEL CO LTD
View PDF5 Cites 33 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The composition of the patented alloy is complex, which is not conducive to cost reduction
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0019] Several examples of the present invention are introduced below, and comparative examples are also given for comparing the effects of the present invention.
[0020]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More
Abstract
The invention discloses a high-carbon and low-alloy steel wire rod for producing fine steel wires, and its manufacturing method. The steel wire rod comprises 0.87-1.1wt% of C, 0.1-1.0wt% of Si, 0.3-1.2wt% of Mn, 0.1-1.0wt% of Cr, 0.015wt% or less of P, 0.010wt% or less of S, 0.0010wt% or less of Ti, 0.0050wt% or less of N, 0.0005-0.0020wt% of total aluminum, 0.0010-0.0030wt% of total oxygen, and the balance Fe and inevitable impurities. The manufacturing method is characterized in that de-oxidation alloying is carried out after converting, and the contents of Al and Ti residual in Si-Fe and Mn-Fe used in the above process are not greater than 0.03%, and the addition amounts of the Si-Fe and the Mn-Fe are 1.5-2.5kg / t and 3.5-4.5kg / t respectively; de-oxidation alloying is carried out in the refining process, the contents of Al and Ti residual in Si-Fe and Mn-Fe used in the refining process are not greater than 0.03%, and the addition amounts of the Si-Fe and the Mn-Fe are 0.5-1.0kg / t and 0.4-0.9kg / t respectively in the refining process; and the content of Al in molten steel in the refining process is 0.0002-0.0015%, and the total oxygen content in the molten steel is 0.0020-0.0040%. The tensile strength of the steel wire rod in the invention is 80-150Mpa higher than that of common 80-grade steel wire rods, the area reduction index is not less than 35%, there is no netted cementite structure, and the length-width ratio of 90% or more of oxide inclusions in the rolling direction is greater than 3, so drawing demands of users are satisfied.
Description
technical field [0001] The invention belongs to the field of low-alloy high-carbon steel, and in particular relates to a high-carbon low-alloy steel wire rod for producing thin steel wires and a manufacturing method thereof. Background technique [0002] It is well known that for high carbon steel wire rod, the tensile strength of the wire rod can be increased by increasing the carbon content. The invention patent entitled "High-strength steel wire rod and high-strength steel wire with excellent fatigue properties (application number) CN94192615.X" provides a high-strength steel wire rod and high-strength steel wire with excellent fatigue properties. Used in steel cords, steel belts and high-strength steel wires; the steel wires are used in steel wire ropes and PC (prestressed concrete) steel wires. The invention patent contains (by mass %) 0.7%-1.1% of C, 0.1%-1.5% of Si, 0.1%-1.5% of Mn, not more than 0.02% of P, not more than 0.02% of S, and others are Fe and unavoidabl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
IPC IPC(8): C22C38/18C22C33/04C21D8/06
Inventor 郭大勇任玉辉臧绍双王长顺王秉喜薛军高航
Owner ANGANG STEEL CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com