Supported non-metallocene catalyst, preparation method and application

A non-metallocene, supported technology, applied in the field of non-metallocene catalysts, can solve the problems of complex preparation process, destruction, complex loading process, etc., and achieve the effect of simple preparation method

Active Publication Date: 2013-03-13
CHINA PETROLEUM & CHEM CORP +1
View PDF39 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods use a magnesium compound support, and the particle morphology of the catalyst is difficult to control, which limits the particle morphology of the polymer obtained from the polymerization.
[0010] Chinese patents CN200910180603.3, CN200910180604.8, CN200910210989.8, CN200910210986.4, CN200910210985.X, CN200910210990.0 disclose the preparation method of supported non-metallocene catalysts similar to the above-mentioned patents. Particle morphology in the presence of catalyst is difficult to control, limiting the polymer particle morphology obtained from this polymerization
[0011] Catalysts supported on anhydrous magnesium chloride show high catalytic activity in olefin polymerization, but such catalysts are very brittle and break easily in the polymerization reactor, resulting in poor polymer morphology
Silica-supported catalysts have good fluidity and can be used in gas-phase fluidized bed polymerization, but silica-supported metallocene and non-metallocene catalysts show low catalytic activity
[0018] Patents CN200910180100.6 and CN200910180607.1 disclose that in the absence of alcohol, the non-metallocene complex is dissolved in the magnesium compound solution, and then the porous carrier is added, dried directly or filtered, washed and dried, and then treated with IVB chemical treatment agents, thereby The preparation method and polymerization application of the supported non-metallocene catalyst are obtained. The non-metallocene complex exists uniformly in the carrier, but in the example...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Supported non-metallocene catalyst, preparation method and application
  • Supported non-metallocene catalyst, preparation method and application
  • Supported non-metallocene catalyst, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0102]The invention relates to a preparation method of a supported non-metallocene catalyst, comprising the following steps: dissolving a magnesium compound in a first solvent to obtain a magnesium compound solution; making a porous carrier optionally subjected to thermal activation treatment and the magnesium contacting the compound solution to obtain a first mixed slurry; adding a precipitant to the first mixed slurry to obtain a composite carrier, contacting the non-metallocene complex with the composite carrier in the presence of a second solvent, a step of obtaining a second mixed slurry; and a step of directly drying the second mixed slurry to obtain the supported non-metallocene catalyst.

[0103] The magnesium compound will be specifically described below.

[0104] According to the present invention, the term "magnesium compound" refers to an organic or inorganic solid anhydrous magnesium-containing compound conventionally used as a carrier of a supported olefin polyme...

Embodiment 1

[0292] The magnesium compound is anhydrous magnesium chloride, the first solvent is tetrahydrofuran, and the porous carrier is silicon dioxide, that is, silica gel, the model is ES757 of Ineos Company, and the silica gel is thermally activated by continuously roasting at 600°C for 4 hours under nitrogen atmosphere before use. The precipitating agent adopts hexane, and the non-metallocene complex adopts the structure The compound, the second solvent adopts dichloromethane.

[0293] Weigh 5g of anhydrous magnesium chloride, add the first solvent and dissolve it completely at room temperature to obtain a magnesium compound solution, then add heat-activated silica gel, and stir at room temperature for 2 hours to form the first mixed slurry. Add the precipitant dropwise to the first mixed slurry, stir and react at 60°C for 4 hours to make it completely precipitate, filter, wash the precipitant twice, each time the amount of precipitant is 60ml, evenly heat to 60°C and vacuum dry ...

Embodiment 1-1

[0298] Basically the same as Example 1, but with the following changes:

[0299] The porous carrier was changed to Grace's 955, and it was continuously calcined at 400° C. for 8 hours under a nitrogen atmosphere to be thermally activated.

[0300] The first solvent is changed to toluene, the precipitant is changed to cyclohexane, and the non-metallocene complex adopts The second solvent was changed to toluene.

[0301] Wherein the ratio is as follows: the ratio of the magnesium compound to the first solvent is 1mol:150ml; the molar ratio of the magnesium compound to the non-metallocene complex is 1:0.15; the mass ratio of the magnesium compound to the porous carrier is 1:4; the precipitating agent and the second A solvent volume ratio of 1:2.

[0302] Supported non-metallocene catalysts are designated CAT-1-1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a supported non-metallocene catalyst and a preparation method. The supported non-metallocene catalyst is prepared by the steps of precipitating a mixed slurry formed by a magnesium compound, a porous carrier and a solvent, and then loading a non-metallocene complex and directly drying; the preparation method is simple and feasible, and the load capacity of the non-metallocene ligand is adjustable. The invention also relates to the application of the supported non-metallocene catalyst in olefin homopolymerisation/copolymerization. Compared with the prior art, the supported non-metallocene catalyst has the characteristics of less usage of a cocatalyst for catalyzing polymerization of alkene, high polymerization activity, narrow molecular weight distribution, substantial copolymerization effect, high bulk density of polymer, and high and adjustable viscosity average molecular weight of the prepared ultrahigh molecular weight polyethylene.

Description

[0001] This application is based on the ongoing research project of "National Eleventh Five-Year Support Program Topics". The project has been highly valued and strongly supported by the Ministry of Science and Technology of the People's Republic of China. Its goal is to form a new generation of polyolefin catalyst technology with independent intellectual property rights, improve the homogeneity of domestic related products, improve the grade of polyolefin varieties in my country, and promote its development. Development in the direction of diversification, serialization, specialization and high performance. technical field [0002] The present invention relates to a non-metallocene catalyst. Specifically, the present invention relates to a supported non-metallocene catalyst, its preparation method and its application in olefin homopolymerization / copolymerization. Background technique [0003] The non-metallocene catalysts that appeared in the mid-to-late 1990s are also call...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F10/00C08F4/02C08F4/658C08F4/653C08F4/654C08F4/656C08F4/655C08F4/646C08F4/645C08F4/649
Inventor 任鸿平李传峰左胜武阚林郭峰梅利柏基业陈韶辉
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap